S-Plastic Geloy FXW710AR ASA injection moulding grade. It is suitable for those applications that require metallic colour e

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Geloy

Product Description

S-Plastics Geloy FXW710AR resin is an ASA injection moulding grade. It is suitable for those applications that require metallic colour effects and good weatherability.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Taber Abrasion, CS-17, 1 kg	155	mg/1000cy	S-Plastics Method
Tensile Stress, yield, 50 mm/min	38	MPa	ISO 527
Tensile Stress, break, 50 mm/min	30	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	2.5	%	ISO 527
Tensile Strain, break, 50 mm/min	4	%	ISO 527
Tensile Modulus, 1 mm/min	1900	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	50	MPa	ISO 178
Flexural Modulus, 2 mm/min	1900	MPa	ISO 178
Hardness, H358/30	70	MPa	ISO 2039-1
Hardness, Rockwell R	95	-	ISO 2039-2
IMPACT	Value	Unit	Standard
Izod Impact, notched 80104 +23°C	12	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	5	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	12	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80104 sp=62mm	4	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Thermal Conductivity	0.21	W/m-°C	ISO 8302
CTE, 23°C to 60°C, flow	9.E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	1.E-04	1/°C	ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	86	°C	ISO 306
Vicat Softening Temp, Rate B/120	91	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	88	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	75	°C	ISO 75/Ae
PHYSICAL	Value	Unit	Standard
Mold Shrinkage on Tensile Bar, flow (2)	0.4 - 0.7	%	S-Plastics Method
Density	1.09	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.55	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.2	%	ISO 62
Melt Volume Rate, MVR at 220°C/10.0 kg	7	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 260°C/5.0 kg	8	cm³/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	>0.E+00	Ohm-cm	IEC 60093
Surface Resistivity, ROA	>0.E+00	Ohm	IEC 60093
Dielectric Strength, in oil, 3.2 mm	16	kV/mm	IEC 60243-1
Relative Permittivity, 50/60 Hz	5.2	-	IEC 60250
Relative Permittivity, 1 MHz	3.2	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.15	-	IEC 60250
Dissipation Factor, 1 MHz	0.026	-	IEC 60250
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94HB Flame Class Rating (3)(4)	1	mm	UL 94 by GE
UL Compliant, 94HB Flame Class Rating 2nd value (3)(4)	3	mm	UL 94 by GE
Glow Wire Flammability Index 750°C, passes at	3.2	mm	IEC 60695-2-12
Oxygen Index (LOI)	19	%	ISO 4589
Source GMD, last updated:06/25/2003

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	75 - 85	°C
Drying Time	2 - 4	hrs
Maximum Moisture Content	0.04	%
Melt Temperature	240 - 260	°C
Nozzle Temperature	220 - 250	°C
Front - Zone 3 Temperature	230 - 260	°C
Middle - Zone 2 Temperature	220 - 250	°C
Rear - Zone 1 Temperature	210 - 240	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	40 - 70	°C
Source GMD, last updated:06/25/2003