S-Plastic Geloy HRE250 High impact,weatherable, flame retardant injection moulding grade Polycarbonate/AES alloy.

Name: S-Plastic Geloy HRE250 High impact,weatherable, flame retardant injection moulding grade Polycarbonate/AES alloy.
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Geloy

Product Description

S-Plastics Geloy HRE250 resin is High impact,weatherable, flame retardant injection moulding grade Polycarbonate/AES alloy.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	59	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	42	MPa	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	120	%	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	90	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2200	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	699	J/m	ASTM D 256
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	120	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	100	°C	ASTM D 648
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.17	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.5 - 0.7	%	S-Plastics Method
Melt Flow Rate, 260°C/5.0 kgf	31	g/10 min	ASTM D 1238
Source GMD, last updated:06/18/1999

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	100	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	8	hrs
Melt Temperature	260 - 280	°C
Mold Temperature	60 - 80	°C
Source GMD, last updated:06/18/1999