Co Extrusion Grade S-Plastic Plastic Injection Pellets Geloy XTWE270M Raw Materials

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Geloy

Product Description

S-Plastics Geloy XTWE270M resin is Excellent weatherability, good flow/aesthetics and good impact.Profile co-extrusion grade over ABS, PVC or other compatible polymers.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	36	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	32	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	3.4	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	38	%	ASTM D 638
Tensile Modulus, 5 mm/min	1910	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	56	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	1830	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	36	MPa	ISO 527
Tensile Stress, break, 50 mm/min	26	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	3.4	%	ISO 527
Tensile Strain, break, 50 mm/min	28	%	ISO 527
Tensile Modulus, 1 mm/min	1790	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	56	MPa	ISO 178
Flexural Modulus, 2 mm/min	1870	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	195	J/m	ASTM D 256
Izod Impact, notched, -30°C	70	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	28	J	ASTM D 3763
Izod Impact, notched 80104 +23°C	13	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	7	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	12	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	85	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	69	°C	ASTM D 648
CTE, -40°C to 40°C, flow	9.2E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	1.09E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	1.E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.16E-04	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	82	°C	ISO 306
Vicat Softening Temp, Rate B/120	85	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	71	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.09	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.3 - 0.7	%	S-Plastics Method
Melt Flow Rate, 220°C/10.0 kgf	9.7	g/10 min	ASTM D 1238
Density	1.09	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.8	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.2	%	ISO 62
Melt Volume Rate, MVR at 220°C/5.0 kg	2	cm³/10 min	ISO 1133
Source GMD, last updated:06/14/2006

Processing

Parameter
Profile Extrusion	Value	Unit
Drying Temperature	85 - 95	°C
Drying Time	8	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	190 - 210	°C
Barrel - Zone 1 Temperature	180 - 200	°C
Barrel - Zone 2 Temperature	180 - 200	°C
Barrel - Zone 3 Temperature	180 - 205	°C
Barrel - Zone 4 Temperature	180 - 205	°C
Hopper Temperature	60 - 80	°C
Adapter Temperature	180 - 205	°C
Die Temperature	185 - 205	°C
Calibrator Temperature	50 - 70	°C
Source GMD, last updated:06/14/2006