Thermoformable S-Plastic Injection Molding Pellets Virgin Plastic Resin Geloy XTWE290

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Geloy

Product Description

S-Plastics Geloy XTWE290 resin is Excellent weathering. Coextrusion capstock grade asa.Thermoformable.Spas and outdoor vehicles.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	55	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	36	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	3	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	15	%	ASTM D 638
Tensile Modulus, 5 mm/min	3000	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	80	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2650	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	53	MPa	ISO 527
Tensile Stress, break, 50 mm/min	35	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	2.8	%	ISO 527
Tensile Strain, break, 50 mm/min	52	%	ISO 527
Tensile Modulus, 1 mm/min	2900	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	74	MPa	ISO 178
Flexural Modulus, 2 mm/min	2600	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	95	J/m	ASTM D 256
Izod Impact, notched, -30°C	35	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	30	J	ASTM D 3763
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	2	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	7	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	89	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	76	°C	ASTM D 648
CTE, -40°C to 40°C, flow	8.5E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	9.5E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	8.5E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	9.5E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	88	°C	ISO 306
Vicat Softening Temp, Rate B/120	90	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	78	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.1	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.35 - 0.7	%	S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm	0.35 - 0.7	%	S-Plastics Method
Melt Flow Rate, 200°C/3.8 kgf	0.5	g/10 min	ASTM D 1238
Density	1.13	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.8	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 220°C/5.0 kg	2	cm³/10 min	ISO 1133
Source GMD, last updated:10/11/2004

Processing

• Barrel temperatures should be banked TO 150°C (300°F)
Parameter
Sheet Extrusion	Value	Unit
Drying Temperature	80 - 90	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	12	hrs
Minimum Moisture Content	0.04	%
Melt Temperature	220 - 245	°C
Barrel - Zone 1 Temperature	180 - 225	°C
Barrel - Zone 2 Temperature	190 - 230	°C
Barrel - Zone 3 Temperature	205 - 240	°C
Barrel - Zone 4 Temperature	210 - 245	°C
Adapter Temperature	210 - 245	°C
Die Temperature	210 - 245	°C
Roll Stack Temp - Top	70 - 100	°C
Roll Stack Temp - Middle	70 - 95	°C
Roll Stack Temp - Bottom	65 - 90	°C
Source GMD, last updated:10/11/2004