S-Plastics Verton KX95702 resin is a compound based on Acetal resin containing Anti-Static. Added features of this material include: Antistat.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	40	MPa	ASTM D 638
Tensile Stress, break	24	MPa	ASTM D 638
Tensile Strain, yield	18.1	%	ASTM D 638
Tensile Strain, break	75.5	%	ASTM D 638
Tensile Modulus, 50 mm/min	1500	MPa	ASTM D 638
Flexural Stress	46	MPa	ASTM D 790
Flexural Modulus	1380	MPa	ASTM D 790
Tensile Stress, yield	41	MPa	ISO 527
Tensile Stress, break	31	MPa	ISO 527
Tensile Strain, yield	14.6	%	ISO 527
Tensile Strain, break	52.4	%	ISO 527
Tensile Modulus, 1 mm/min	1110	MPa	ISO 527
Flexural Stress	35	MPa	ISO 178
Flexural Modulus	1350	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D 4812
Izod Impact, notched, 23°C	160	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	22	J	ASTM D 3763
Multiaxial Impact	16	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	14	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	78	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.24E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	1.39E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	1.24E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.39E-04	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	64	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.32	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	4.05	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	1.7	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1.8	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	1.74	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.83	%	ISO 294
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+09 - 1.E+11	Ohm	ASTM D 257
Source GMD, last updated:10/01/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	195 - 205	°C
Front - Zone 3 Temperature	200 - 210	°C
Middle - Zone 2 Temperature	190 - 200	°C
Rear - Zone 1 Temperature	175 - 190	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:10/01/2004