Product Description

S-Plastics Verton PF006I resin is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	142	MPa	ASTM D 638
Tensile Stress, yld, Type I, 5 mm/min	50	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	97	MPa	ASTM D 638
Tensile Strain, break	3.2	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	8.1	%	ASTM D 638
Tensile Modulus, 50 mm/min	16230	MPa	ASTM D 638
Flexural Stress	211	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	157	MPa	ASTM D 790
Flexural Modulus	6550	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	6820	MPa	ASTM D 790
Tensile Stress, break	138	MPa	ISO 527
Tensile Stress, yield, 5 mm/min	35	MPa	ISO 527
Tensile Stress, break, 5 mm/min	99	MPa	ISO 527
Tensile Strain, break	8.1	%	ISO 527
Tensile Modulus, 1 mm/min	9650	MPa	ISO 527
Flexural Stress	148	MPa	ISO 178
Flexural Modulus	6510	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	727	J/m	ASTM D 4812
Izod Impact, notched, 23°C	106	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	16	J	ASTM D 3763
Multiaxial Impact	4	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	53	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	10	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	139	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	137	°C	ASTM D 648
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	141	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	135	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.35	-	ASTM D 792
Density	1.35	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.83	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.1 - 0.3	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.9 - 2	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.11 - 0.3	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.62 - 0.67	%	ISO 294
Density	1.37	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.83	%	ISO 62
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94HB Flame Class Rating (3)(4)	1.5	mm	UL 94 by GE
Source GMD, last updated:10/02/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	265 - 275	°C
Front - Zone 3 Temperature	275 - 290	°C
Middle - Zone 2 Temperature	265 - 275	°C
Rear - Zone 1 Temperature	250 - 260	°C
Mold Temperature	80 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:10/02/2004