S-Plastic Verton W3000 is a compound based on Polybutylene Terephalate resin containing Anti-Static. Added features of this

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Verton

Product Description

S-Plastics Verton W3000 resin is a compound based on Polybutylene Terephalate resin containing Anti-Static. Added features of this material
include: Antistat.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	41	MPa	ASTM D 638
Tensile Stress, break	40	MPa	ASTM D 638
Tensile Strain, yield	8.2	%	ASTM D 638
Tensile Strain, break	14.6	%	ASTM D 638
Tensile Modulus, 50 mm/min	1580	MPa	ASTM D 638
Flexural Stress	59	MPa	ASTM D 790
Flexural Modulus	1720	MPa	ASTM D 790
Tensile Stress, yield	37	MPa	ISO 527
Tensile Stress, break	37	MPa	ISO 527
Tensile Strain, yield	10.9	%	ISO 527
Tensile Strain, break	12.7	%	ISO 527
Tensile Modulus, 1 mm/min	1630	MPa	ISO 527
Flexural Stress	58	MPa	ISO 178
Flexural Modulus	1640	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	1254	J/m	ASTM D 4812
Izod Impact, notched, 23°C	58	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	32	J	ASTM D 3763
Multiaxial Impact	3	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	137	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	46	°C	ASTM D 648
PHYSICAL	Value	Unit	Standard
Density	1.27	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.65	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	1.7	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	2	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	1.74	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.99	%	ISO 294
Density	1.27	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	1.09	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+09 - 1.E+11	Ohm	ASTM D 257
Source GMD, last updated:10/01/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	110	°C
Drying Time	4	hrs
Maximum Moisture Content	0.05	%
Melt Temperature	220 - 230	°C
Front - Zone 3 Temperature	220 - 230	°C
Middle - Zone 2 Temperature	215 - 225	°C
Rear - Zone 1 Temperature	205 - 215	°C
Mold Temperature	10 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:10/01/2004