LNP™ LUBRICOMP™ COMPOUND C2801 Compound Is Based On Polycarbonate Acrylonitrile Butadiene Styrene (PC/ABS) Blend

Price Negotiable

Price: *USD to be negotiated

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic

Product Description

LNP LUBRICOMP C2801 compound is based on Polycarbonate / Acrylonitrile Butadiene Styrene (PC/ABS) blend containing 5% PTFE. Added features of this grade include: Wear Resistant and Flame Retardant targeted for moving components in business equipment. Medium Heat performance.

Property

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
(1) MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	62	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	51	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	110	%	ASTM D638
Flexural Stress, yld, 2.6 mm/min, 100 mm span	95	MPa	ASTM D790
Flexural Modulus, 2.6 mm/min, 100 mm span	2720	MPa	ASTM D790
K-factor xE-10, PV=2000 psi-fpm vs Steel	430	-	S-Plastics method
Coefficient of Friction on steel, Static	0.16	-	ASTM D1894
Coefficient of Friction on steel,Kinetic	0.21	-	ASTM D1894
(1)IMPACT
Izod Impact, notched, 23°C	133	J/m	ASTM D256
(1)THERMAL
HDT, 1.82 MPa, 6.4 mm, unannealed	82	°C	ASTM D648
(2)Relative Temp Index, Elec	60	°C	UL 746B
(2)Relative Temp Index, Mech w/impact	60	°C	UL 746B
(2) Relative Temp Index, Mech w/o impact	60	°C	UL 746B
(1)
PHYSICAL
Specific Gravity	1.22	-	ASTM D792
(3) Mold Shrinkage, flow, 3.2 mm	0.4 – 0.5	%	S-Plastics method
(3) Mold Shrinkage, xflow, 3.2 mm	0.3 – 0.5	%	S-Plastics method
PROPERTIES(1) ELECTRICAL	TYPICAL VALUES	UNITS	TEST METHODS
Comparative Tracking Index (UL) {PLC}	1	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 3	≥1.5	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 0	≥1.5	mm	UL 746A
(2) FLAME CHARACTERISTICS
UL Yellow Card Link	E121562-221032	-	-
UL Yellow Card Link 2	E207780-228469	-	-
UL Recognized, 94-5VB Flame Class Rating	≥2.5	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating	≥1.5	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating	≥1	mm	UL 94

Processing

Drying Temperature	75 – 80	°C
Drying Time	3 – 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.04	%
Melt Temperature	230 – 275	°C
Nozzle Temperature	230 – 275	°C
Front - Zone 3 Temperature	225 – 275	°C
Middle - Zone 2 Temperature	215 – 260	°C
Rear - Zone 1 Temperature	210 – 255	°C
Mold Temperature	50 – 70	°C
Back Pressure	0.3 – 0.7	MPa
Screw Speed	40 – 70	rpm
Shot to Cylinder Size	30 – 80	%
Vent Depth	0.038 – 0.076	mm

For more information please download the datesheet
	LNP LUBRICOMP C2801.pdf

Get The Latest Quotation

First-level distribution source in South China
Reduce procurement costs, improve supply stability,
Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!