Anti Oxidation 310S Stainless Steel Plate , PVC Laser Film 8K Stainless Steel Sheet
310S NO.8 8K Mirror Finish Stainless Steel Plate with PVC laser Film
Product Description
310S stainless steel plate is a 25Cr-20Ni high alloy stainless steel with excellent high-temperature oxidation resistance.
It is suitable for making various furnace components with a maximum temperature of 1200 ℃ and a continuous service temperature of 1150 ℃.
Product Diaplay
| Chemicai Composition(WT%) | ||||||||
| Grade | (C) | (Si) | (Mn) | (Cr) | (N) | (Ni) | (P) | (S) |
| 310S | ≤0.08 | ≤1.5 | ≤2.0 | 24.0~26.0 | ≤0.1 | 19.0~22.0 | ≤0.045 | ≤0.030 |
| Physical Property | ||||||||
| yield strength(mpa) | magnetic | extend(%) | ||||||
| ≥205 | non | ≥40 | ||||||
|
Application |
||||||||
| furnace materials, automobile purification device materials | ||||||||
Tolerance Standard Range
| 310S/Cold | ||||
| Thickness | Large Tolerance | Normal | Close Tolerance | No Tolerance |
| 0.4MM | 0.3-0.32 | 0.33-0.37 | 0.37-0.39 | 0.39 Above |
| 0.5MM | 0.4-0.42 | 0.43-0.47 | 0.47-0.49 | 0.49 Above |
| 0.6MM | 0.5-0.52 | 0.53-0.56 | 0.57-0.59 | 0.59 Above |
| 0.7MM | 0.6-0.62 | 0.63-0.67 | 0.67-0.69 | 0.69 Above |
| 0.8MM | 0.7-0.72 | 0.73-0.77 | 0.74-0.79 | 0.79 Above |
| 0.9MM | 0.8-0.82 | 0.83-0.87 | 0.87-0.89 | 0.89 Above |
| 1.0MM | 0.89-0.9 | 0.91-0.94 | 0.94-0.99 | 0.99 Above |
| 1.2MM | 1.02-1.08 | 1.09-1.15 | 1.16-1.18 | 1.18 Above |
| 1.5MM | 1.32-1.38 | 1.39-1.45 | 1.46-1.48 | 1.48 Above |
| 2.0MM | 1.72-1.79 | 1.8-1.86 | 1.87-1.9 | 1.9 Above |
| 2.5MM | 2.23-2.36 | 2.32-2.42 | 2.42-2.47 | 2.48 Above |
| 3.0MM | 2.7-2.77 | 2.78-2.85 | 2.85-2.9 | 2.9 Above |
| 310S/Hot | ||||
| Thickness | Large Tolerance | Normal | Close Tolerance | No Tolerance |
| 3.0MM | 2.6-2.75 | 2.75-2.85 | 2.86-2.9 | 2.9 Above |
| 4.0MM | 3.5-3.6 | 3.6-3.75 | 3.76-3.95 | 3.95 Above |
| 5.0MM | 4.5-4.6 | 4.6-4.75 | 4.75-4.95 | 4.95 Above |
| 6.0MM | 5.4-5.6 | 5.6-5.75 | 5.75-5.85 | 5.85 Above |
| 8.0MM | 7.3-7.5 | 7.5-7.65 | 7.65-7.85 | 7.85 Above |
| 10.0MM | 9.2-9.3 | 9.3-9.6 | 9.6-9.85 | 9.85 Above |
| 12.0MM | 11.1-11.2 | 11.2-11.6 | 11.6-11.85 | 11.85 Above |
| 14.0MM | 13.1-13.2 | 13.2-13.6 | 13.6-13.85 | 13.85 Above |
Advantage
1.310S stainless steel is austenitic chromium nickel stainless steel with good oxidation resistance and corrosion resistance.
2.Because of the high percentage of chromium and nickel, it has much better creep strength,can work continuously at high temperature, and has good high temperature resistance.
3.Because of the high content of nickel (Ni) and chromium (CR), it has good oxidation resistance, corrosion resistance,acid and alkali resistance and high temperature resistance. High temperature resistant steel pipes are specially used for manufacturing electric furnace tubes and other occasions. After the carbon content is increased in austenitic stainless steel,the strength is improved due to its solid solution strengthening effect. The chemical composition characteristics of austenitic stainless steel are based on chromium and nickel, and molybdenum, tungsten, niobium and titanium are added.
4.Because its structure is face centered cubic structure, And thus has high strength and creep strength at high temperature.