Cold Rolled AISI434 / EN 1.4113 Stainless Steel Sheets & Plate 0.4 - 3.0mm Thickness
Cold Rolled AISI434 / EN 1.4113 Stainless Steel Sheets & Plate 0.4 - 3.0mm Thickness
Products Specification
| Products Name | AISI434 Stainless Steel Sheet |
| Standard | ASTM EN JIS GB BIS |
| Thickness |
0.4mm 0.5mm 0.6mm 0.8mm 1.0mm 1.2mm 1.5mm 2.0mm 2.5mm 3.0mm |
| Surface | 2B 2D NO.1 or process other surface as request |
| Standard Size | 1219*2438mm 1000*2000mm |
| Service | Slit Cutting, bending , surface treatment |
| Other Grade | 200 Series: 201 202 |
| 300 Series: 301 304 304L 309S 310S 316L 316Ti 317l 321 329 347 | |
| 400 Series: 409L 410S 416 420 431 436L 439 441 443 444 446 | |
| Special Grade: 254SMO 904L 2205 2507 253MA Nickel Alloy | |
| MOQ | 500 kgs |
| Packing | Wooden Pallets and waterproof paper |
Stainless steels are high-alloy steels. They have high corrosion resistance due to high chromium content of about 4-30%. They are classified in to three types such as ferritic, austenitic, and martensitic steels based on their crystalline structure.
Grade 434 stainless steel contains added molybdenum to increase its corrosion resistance. It is has performance and chemistry similar to that of 430 stainless steel.
Chemical Composition
The following table shows the chemical composition of grade 434 stainless steel.
| Grade | C | Si | Mn | P | S | Cr | Mo | Fe |
| AISI434 / EN 1.4113 | 0.12 | 1.00 | 1.00 | 0.04 | 0.03 | 16.0-18.00 | 0.8-1.25 | Bal |
Mechanical Properties
The following table outlines the mechanical properties of annealed grade 434 stainless steel.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 538 MPa | 78000 psi |
| Yield strength (@ strain 0.200%) | 441 MPa | 64000 psi |
| Elastic modulus | 200 GPa | 29008 ksi |
| Poisson's ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 32% | 32% |
| Hardness, Rockwell B (converted from Brinell hardness) | 89 | 89 |
Other designations that are equivalent to grade 434 stainless steel include:
- DIN 1.4113
- AFNOR Z 8 CD 17.01
- UNI X 8 CrMo 17
- JIS SUS 434
- SS 2325
- B.S. 434 S 19
- ASTM A65i
- SAE 51434
- SAE J405 (51434)
Machinability
Grade 434 stainless steel can be machined using all standard procedures.
Forming
Blanking, shearing, and deep drawing operations can be successfully performed due to its high ductility.
Welding
Grade 434 stainless steel can be welded using common techniques. After welding, it should be thoroughly cleaned to increase corrosion resistance property.
Forging
Grade 434 stainless steel can be forged at 1094 -1149°C (2000-2100°F) after thorough soaking.
Annealing
Grade 434 stainless steel is annealed by soaking at 788 - 872°C (1450-1600°F) followed by cooling in air.
Hardening
Grade 434 stainless steel does not react to heat treatment.