Heat Resistant 310H Stainless Steel Plate AISI310H 3.0 - 40.0mm in 1500mm Width from TISCO
Heat Resistant 310H Stainless Steel Plate AISI310H 3.0 - 40.0mm in 1500mm Width from TISCO
More Informations of our Products
|
Product
|
Stainless Steel Sheet/Plate
|
|
Standard
|
ASTM A240,GB/T3280-2007,JIS4304-2005,ASTM A167,EN10088-2-2005,etc
|
|
Material
|
310S,310,310H,309,309S,316,316L,316Ti,317,317L,321,321H,347,347H,304,304L,302,301,
201,202,403,405,409,409L,410,410S,420,430,631,904L,Duplex,etc
|
|
Surface
|
2B,2D,BA,NO.1,NO.4,NO.8,8K,mirror,checkered,embossed,hair line,sand blast,Brush
|
|
Thickness
|
Cold Rolled:0.3-6mm
|
|
Hot Rolled: 3-20mm
|
|
|
Width
|
1000mm,1219mm,1500mm,1800mm,2000mm,2500mm,,etc
|
|
Length
|
2000mm,2440mm,3000mm,5800mm,6000mm,etc
|
|
Package
|
Covered with a layer of plastic film and cardboard,packed on the wooden pallets/ iron packing,bound with iron belt,loaded in the containers.
|
|
Price Terms
|
Ex-Work,FOB,CFR,CIF,FCA,etc
|
|
Payment Terms
|
TT,L/C at sight ,western Union,etc.
|
Stainless steel grade 310H has carbon content and is a preferred choice for high temperature applications. This steel has good resistance to oxidation at temperatures of up to 1040°C (1904°F) in intermittent service and 1150°C (2102°F) in continuous service. It is widely used in environments where sulfur dioxide gas is present at high temperatures; however it is recommended that this steel should not be continuously used at 425-860°C (797-1580°F) range due to carbide precipitation.
The following datasheet provides an overview of stainless steel grade 310H.
310H Stainless Steel Plate We Have Stock
| 3.0*1500*6000mm | 4.0*1500*6000mm | 5.0*1500*6000mm | 6.0*1500*6000mm |
| 8.0*1500*6000mm | 10.0*1500*6000mm | 12.0*1500*6000mm | 14.0*1500*6000mm |
| 15.0*1500*6000mm | 16.0*1500*6000mm | 18.0*1500*6000mm | 20.0*1500*6000mm |
| 22.0*1500*6000mm | 25.0*1500*6000mm | 30.0*1500*6000mm | 32.0*1500*6000mm |
| 35.0*1500*6000mm | 38.0*1500*6000mm | 40.0*1500*6000mm |
Chemical Composition OF 310H Stainless Steel Plate
The chemical composition of grade 310H stainless steel is outlined in the following table.
| Element | Content (%) |
|---|---|
| Iron, Fe | 49.075-45.865 |
| Chromium, Cr | 24-26 |
| Nickel, Ni | 19-22 |
| Manganese, Mn | 2 |
| Silicon, Si | 0.75 |
| Phosphorous, P | 0.045 |
| Carbon, C | 0.040-0.10 |
| Sulfur, S | 0.03 |
Mechanical Properties of 310H Stainless Steel Plate
The mechanical properties of annealed grade 310H stainless steel are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 515 MPa | 74694 psi |
| Yield strength | 205 MPa | 29732 psi |
| Modulus of elasticity | 200 GPa | 29000 ksi |
| Shear modulus | 77.0 GPa | 11200 ksi |
| Poissons ratio | 0.3 | 0.3 |
| Elongation at break (in 50 mm) | 40% | 40% |
| Hardness, Rockwell B | 95 | 95 |
| Hardness, Brinell | 217 | 217 |
Applications of 310H Stainless Steel Plate
Grade 310H stainless steel is chiefly used in the heat treatment industry, and the chemical process industry.
The following are the specific areas of applications:
- Fans
- Trays
- Baskets
- Rollers
- Burner parts
- Oven linings
- Tube hangers
- Retorts linings
- Conveyor belts
- Refractory supports
- Containers for hot concentrated acids, ammonia, and sulfur dioxide
- Used along with hot acetic and citric acid in the food processing industry.