GH2132 US Standard Unss66286 Nickel Base Alloy Round Bar Solid Solution Finishing
GH2132 (US standard unss66286) Nickel Base Alloy Round Bar Solid Solution Finishing
| Form | Nickel Alloy Bars |
| Grade | GH2132 |
| Outer Diameter | 6mm-300mm or according to customer’s requirement |
| Length | custom cutting any length as request |
| Standard | ASTM, ASME, EN, JIS, DIN, GB/T, etc |
| Process Method | Hot Rolled, Cold Drawn, Cold Rolled, Forged Round Bar & Rod |
| Surface Finish | Bright, Hot Rolled Pickled, Cold Drawn, Sand Blasting Finished, Polished, Hairline |
| Other Grade |
Hastelloy : B2 B3 C22 C276 G30 X Incoloy: 800 800H 800HT 825 925 A286 330 Inconel: 600 601 617 625 718 725 X-750 Monel: 400 k-500 |
| Price Item | EXW FOB CFR CIF |
| Payment | 30% TT inadvance, 70% TT Balance against copy of B/L |
| Delivery Time | It depends on your bars order total quantity and stock of these mother origin materials. Usually from the start of the order to the completion of production is about 3-4 weeks |
| Quality Requirement | Mill test certificate will be offered with shipment, the third party inspection is available |
| Main Markets | Europe, North America, Middle East, Southeast Asia |
| Metal Test | High or low temperature impact test, metallographic analysis |
| Chemical Analysis | As nickel alloy 718 bars standard |
Our Service
- Cutting: custom cutting our bars into any length as request
- Polishing: Bright polishing , cold drawn finishing
- Heat Treatment: Solid Solution , aging, Q+T
Chemical composition of GH2132:
| % | nickel | chromium | molybdenum | boron | iron | aluminum | titanium | carbon | manganese | silicon | vanadium | sulfur | |
| GH2132 | minimum | 24 | 13.5 | 1.0 | 0.001 | more than | 1.75 | 1.0 | 0.10 | ||||
| maximum | 27 | 16 | 1.5 | 0.01 | amount | 0.40 | 2.35 | 0.08 | 2.0 | 1.0 | 0.50 | 0.02 |
Physical properties of GH2132:
| density | 7.93 g/cm3 |
| melting point | 1364-1424℃ |
Mechanical properties of GH2132 alloy in solution state at room temperature:
| Alloy state | tensile strengthσb (Mpa) | yield strengthσ0.2 (Mpa) | ElongationA5 % |
| GH2132 | ≥950 | ≥680 | ≥28 |
The main characteristics of this alloy are as follows:
Under 650 ° C, it has high yield strength, long-lasting and creep strength, and has good processing plasticity and satisfactory welding performance.
Application example: high temperature bearing parts of aeroengine, such as turbine wheel, etc., which work for a long time under 650 ° C
Metallographic structure of GH2132
Under the standard heat treatment condition, GH2132 alloy has spherical and uniformly dispersed Ni 3 (Ti, Al) type γ phase, tin, tic, and micro m3b2 on the grain boundary. There may be a small amount of η phase and L phase near the grain boundary
Applications of GH2132 include:
It is a kind of alloy material with high temperature strength and high temperature oxidation resistance
1. It is widely used in the manufacturing of parts and components of aeroengines and industrial gas turbines, such as turbine blades, afterburner, fasteners, etc
2. It is also widely used in automobile engines
Products of our company:
Cold and hot plate, strip, tube, wire, forging bar, hot rolling bar, machined products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.