ASTM A240 410 Stainless Steel Sheet Cold Rolled with Polished Surface for Industrial Applications
Price:
US $1.35-2 / kg
MOQ:
50 kg
Delivery Time:
Negotiable
Product Description
1Cr13 Inox Sheet ASTM A240 410 Stainless Steel Sheet
410 Stainless Steel Properties
Type 410 stainless steel is a hardenable, martensitic stainless steel that combines superior wear resistance with excellent corrosion resistance. This grade features high strength, heat resistance, and good ductility, making it well-suited for highly stressed parts in mild atmospheres, steam, and mild chemical environments. Grade 410 is magnetic in both annealed and hardened conditions.
Our 410 stainless steel materials are used in aerospace, automotive, petrochemical, and medical applications. This grade is also ideal for manufacturing springs, fasteners, and other components that require machining after tempering or annealing.
Standard Inventory Specifications
UNS S41000 AMS 5504 AMS 5613 (Chemistry only)
ASTM A 240 ASTM A 276 ASTM A 493
ASTM F 899 ASME SA 240 B50991B
ASTM A 240 ASTM A 276 ASTM A 493
ASTM F 899 ASME SA 240 B50991B
Chemical Composition
| Element | Percent by Weight |
|---|---|
| Carbon (C) | 0.15 max |
| Manganese (Mn) | 1.00 max |
| Silicon (Si) | 1.00 max |
| Chromium (Cr) | 11.50 - 13.50 |
| Nickel (Ni) | 0.75 max |
| Sulfur (S) | 0.03 max |
| Phosphorus (P) | 0.04 max |
Physical Properties
- Density: 0.276 lb/in³
- Specific Gravity: 7.65
- Melting Range: 2700-2790°F (1482-1532°C)
- Modulus of Elasticity: 29 x 10⁶ psi (200 GPa)
Coefficient of Thermal Expansion
| Temperature Range | Coefficients |
|---|---|
| 20-200°C (68-392°F) | 10.5 x 10⁻⁶ cm/cm/°C (5.9 x 10⁻⁶ in/in/°F) |
| 20-600°C (68-1112°F) | 11.6 x 10⁻⁶ cm/cm/°C (6.5 x 10⁻⁶ in/in/°F) |
Thermal Conductivity
| Temperature | W/m·K | Btu/(hr · ft · °F) |
|---|---|---|
| 100°C (212°F) | 0.249 | 14.4 |
Specific Heat
0.11 Btu/lb·°F
Electrical Resistivity
| Temperature | microhm-cm |
|---|---|
| 20°C (68°F) | 56 |
Mechanical Properties and Yield Strength
| Typical Annealed Properties | Hardening Response HRC |
|---|---|
|
HRB: 82-96 0.2% Offset Yield Strength: 30-42 Ksi (205-290 MPa) Tensile Strength: 65-74 Ksi (450-510 MPa) Elongation: 20-34% in 2" (51 mm) |
38-45 |
Common Trade Names
- ATI 410 (™ Allegheny Technologies)
- Alloy 410
- AISI Type 410
Common Applications
- Aerospace structures
- Automotive exhausts, manifolds and high temperature engine components
- Medical instruments and devices
- Petro-chemical applications
- Cutlery and kitchen utensils
- Flat springs
- Hand tools
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
Location
No.283-1, Youyi Middle Road, Xishan District, Wuxi City, Jiangsu Province
Contact Person
Gao Ben