Corrosion Resistant SS 316L Stainless Steel Sheet Cold Rolled with Bright Surface Finish
Price:
US $1.65-4.85 / kg
MOQ:
50 kg
Delivery Time:
Negotiable
Product Description
Type 316 Austenitic Stainless Steel Sheets
316/316L Stainless Steel Sheet is a premium grade where superior corrosion resistance is essential. This material is widely used in marine environments, highly acidic conditions, underwater equipment, surgical tools, and food/pharmaceutical applications. The molybdenum addition enhances corrosion resistance compared to the more economical 304 grade.
Product Forms & Specifications
Available Forms
Sheet, Plate, Coil, Strip, Wire, Pipe, Tube, Bar, Profile, Round, Flat, Square, Hexagonal
Specifications
AMS 5507, AMS 5524, AMS 5648, AMS 5653, ASME SA 240, ASME SA 312, ASME SA 479, ASTM A 240, ASTM A 276, ASTM A 276 Condition A, ASTM A 276 Condition S, ASTM A 312, ASTM A 479, EN 1.4404, W. Nr./EN 1.4401, Werkstoff 1.4401, Werkstoff 1.4404
| Product Type | SS 316 Sheet, SS 316 Plate |
|---|---|
| Material Grade | ASTM A240 / ASME SA240 Grade 316 |
| Tolerances | EN 10258/ DIN 59381, EN 10151, EN 10088 |
| Standards | ASTM A 480, ASTM A 959, ASME IID, EN ISO 9445, EN ISO 18286, EN 10051, EN 10088-1, ISO 15510 |
| Available Sizes | Cold rolled: 0.5-6.4 mm, Hot rolled: 3.0-10.0 mm |
| Thickness | 0.1 to 100 mm |
| Width | 10-2500 mm |
| Length | 2m, 2.44m, 3m, or as required |
| Finish | 2B, 2D, BA NO (8), CR, HR, SATIN, No.1, 1D, No.4, BA, 8K, satin, hairline, brush, mirror, etc. |
| Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard |
| Form | Plate, Sheet, Coils, Foils, Strip, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle) |
Dimension Ranges
Width: 600mm - 2030 mm
Thickness: 0.1 - 120.0 mm
Length: 300 - 6000 mm, Maximum 18000 mm
Thickness: 0.1 - 120.0 mm
Length: 300 - 6000 mm, Maximum 18000 mm
Surface Finishes
No.1, 2B, BA, No.3, No.4, No.5, No.8, HL, Etching, SB, Ti-coating, color-coating, embossing
Applications
- Food processing equipment
- Marine applications
- Surgical instruments
- Firearms production
- Pulp & paper industry
- Chemical process vessels
- Pharmaceutical equipment
Technical Data - Chemical Composition
| Element | Type 316 (wt %) | Type 316L (wt %) |
|---|---|---|
| Carbon (C) | 0.08 max. | 0.03 max. |
| Manganese (Mn) | 2.00 max. | 2.00 max. |
| Phosphorus (P) | 0.045 max. | 0.045 max. |
| Sulfur (S) | 0.030 max. | 0.03 max. |
| Silicon (Si) | 0.75 max. | 0.75 max. |
| Chromium (Cr) | 16.00 - 18.00 | 16.00 - 18.00 |
| Nickel (Ni) | 10.00 - 14.00 | 10.00 - 14.00 |
| Molybdenum (Mo) | 2.00 - 3.00 | 2.00 - 3.00 |
| Nitrogen (N) | 0.10 max. | 0.10 max. |
| Iron (Fe) | Balance | Balance |
Mechanical Properties
Typical Room Temperature Mechanical Properties
| UTS ksi (MPa) | 0.2% YS ksi (MPa) | Elongation % in 2" | Rockwell Hardness |
|---|---|---|---|
| 91 (627) | 42 (290) | 55 | B79 |
Elevated Temperature Mechanical Properties
| Temperature °F (°C) | UTS ksi (MPa) | 0.2% YS ksi (MPa) | Elongation % in 2" |
|---|---|---|---|
| 400 (204) | 81 (558) | 35 (241) | 51 |
| 600 (316) | 78 (538) | 31 (214) | 48 |
| 800 (427) | 76 (524) | 28 (190) | 47 |
| 1000 (538) | 70 (483) | 24 (165) | 44 |
| 1200 (649) | 57 (393) | 21 (145) | 40 |
| 1400 (760) | 35 (241) | 18 (124) | 37 |
| 1600 (871) | 24 (165) | 16 (110) | 44 |
Physical Properties & Processing
Corrosion Resistance
Types 316 and 316L exhibit improved chloride corrosion resistance compared to Type 304 due to molybdenum addition. Provides excellent protection in marine atmospheres and good chemical resistance in paper, petroleum, food, and dairy industries. Suitable for sulfuric acid environments below 5% concentration up to 150°F (60°C). Excellent resistance to acetic, formic, phosphoric, and tartaric acids.
Heat Treatment
Annealing: Heat to 1900-2100°F (1038-1149°C), then rapidly quench.
Cold Working
Work hardens at lower rate than Type 304. Excellent ductility in annealed condition for roll forming, deep drawing, and bending. Annealing essential to restore ductility and lower hardness for subsequent forming operations.
Weldability
Austenitic stainless steels are generally weldable by common fusion and resistance techniques. Type 316/316L requires slower arc welding speeds and more care to avoid hot cracking due to higher nickel content. Recommended filler materials: AWS E/ER 316L and 16-8-2.
Product Images
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
Location
No.283-1, Youyi Middle Road, Xishan District, Wuxi City, Jiangsu Province
Contact Person
Gao Ben