253MA UNS S30815 Stainless Steel Plate with High Temperature Resistance Hot Rolled and Polished Surface
Price:
US $3.65-8.85 / kg
MOQ:
100 kg
Delivery Time:
Negotiable
Product Description
253MA Stainless Steel Plate - UNS S30815
253MA is a high-temperature stainless steel grade combining excellent service properties with ease of fabrication. It resists oxidation at temperatures up to 1150°C and provides superior performance to Grade 310 in carbon, nitrogen, and sulphur-containing atmospheres.
Key Features and Benefits
- Excellent oxidation resistance up to 1150°C
- Superior performance in carbon, nitrogen, and sulphur atmospheres
- Good oxide stability and high elevated temperature strength
- Excellent resistance to sigma phase precipitation
- Maintains toughness even at cryogenic temperatures
- Lower nickel content provides advantage in reducing sulphide atmospheres
Specifications and Standards
ASME SA 182, ASME SA 213, ASTM A 240, ASTM A 276, ASTM A 312, ASTM A 479, UNS S30815, Werkstoff 1.4835
Common Stainless Steel Grade Comparison
| ASTM | JIS | AISI | EN |
|---|---|---|---|
| S30100 | SUS301 | 301 | 1.431 |
| S30400 | SUS304 | 304 | 1.4301 |
| S30403 | - | 304L | 1.4307 |
| S31008 | SUS310S | 310S | 1.4845 |
| S31603 | - | 316L | 1.4404 |
| S32100 | SUS321 | 321 | 1.4541 |
| S41008 | SUS410S | 410S | - |
| S43000 | SUS430 | 430 | 1.4016 |
| S43932 | - | - | 1.451 |
| S44400 | SUS444 | 444 | 1.4521 |
| S44500 | SUS430J1L | - | - |
Available Dimensions
- Width: 600mm - 2030mm
- Thickness: 0.1mm - 120.0mm
- Length: 300mm - 6000mm (Maximum: 18000mm)
Surface Finish Options
No.1, 2B, BA, No.3, No.4, No.5, No.8, HL, Etching, SB, Ti-coating, color-coating, embossing
Typical Applications
- Furnace components including burners, retorts, conveyor belts
- Fans, jigs and baskets, rollers, walking beams
- Radiant tubes, electric heater elements, refractory anchors
- Hoods, flues, grates, expansion bellows
- Petrochemical and refinery tube hangers
Equivalent Materials
| ASTM A182 Grade FXM-19 | ASTM A269 Grade TPXM-19 | ASTM A580 Grade S20910 |
|---|---|---|
| ASTM A193 Grade B8R Class 1C | ASTM A276 Grade S20910 | ASTM A813 Grade TPXM-19 |
| ASTM A193 Grade B8R Class 1D | ASTM A312 Grade TPXM-19 | ASTM A814 Grade TPXM-19 |
| ASTM A193 Grade B8RA Class 1C | ASTM A314 Grade S20910 | ASTM A943 Grade TPXM-19 |
| ASTM A194 Grade 8R | ASTM A336 Grade FXM-19 | ASTM A959 Grade S20910 |
| ASTM A194 Grade 8RA | ASTM A358 Grade A240 XM-19 | ASTM A965 Grade FXM-19 |
| ASTM A213 Grade XM-19 | ASTM A403 Grade CRXM-19 | AISI XM-19 |
| ASTM A240 Grade S20910 | ASTM A403 Grade WPXM-19 | SAE XM-19 |
| ASTM A249 Grade TPXM-19 | ASTM A479 Grade S20910 | UNS S20910 |
Chemical Composition
Typical compositional ranges for 253MA stainless steel:
| Element | Min (%) | Max (%) |
|---|---|---|
| C | 0.05 | 0.10 |
| Mn | - | 0.80 |
| Si | 1.10 | 2.00 |
| P | - | 0.040 |
| S | - | 0.030 |
| Cr | 20.0 | 22.0 |
| Ni | 10.0 | 12.0 |
| N | 0.14 | 0.20 |
| Ce | 0.03 | 0.08 |
Mechanical Properties
| Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Rockwell B (HR B) max | Brinell (HB) max |
|---|---|---|---|---|
| 600 | 310 | 40 | 95 | 217 |
Physical Properties
| Property | Value |
|---|---|
| Density (kg/m³) | 7800 |
| Elastic Modulus (GPa) | 200 |
| Mean Coefficient of Thermal Expansion (mm/m/°C) 0-100°C | 17.0 |
| Mean Coefficient of Thermal Expansion (mm/m/°C) 0-600°C | 18.5 |
| Mean Coefficient of Thermal Expansion (mm/m/°C) 0-1000°C | 19.5 |
| Thermal Conductivity (W/m.K) at 20°C | 15.0 |
| Thermal Conductivity (W/m.K) at 1000°C | 29.0 |
| Specific Heat 0-100°C (J/kg.K) | 500 |
| Electrical Resistivity (nW.m) | 850 |
International Grade Comparisons
| UNS No | Euronorm No | Euronorm Name | Swedish SS | Japanese JIS |
|---|---|---|---|---|
| S30815 | 1.4835 | X9CrNiSiNCe21-11-2 | 2368 | - |
These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed, original specifications must be consulted.
Possible Alternative Grades
| Grade | Why it might be chosen instead of 253MA |
|---|---|
| 310 | Carburising atmospheres require a higher nickel content |
| 304H | Lower cost alternative, provided the operating temperature is below about 800°C |
| Nickel Alloys | Carburising atmospheres or temperatures above the 1100-1150°C maximum of 253MA |
Product Images
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
Location
No.283-1, Youyi Middle Road, Xishan District, Wuxi City, Jiangsu Province
Contact Person
Gao Ben