Hot Rolled Bright Surface 17-4PH Stainless Steel Rod with OD 6-300mm
Price:
US $1.85-10.85 / kg
MOQ:
50 kg
Delivery Time:
Negotiable
Product Description
630 Stainless Steel 17-4PH Rod
17-4PH Precipitation Hardening Stainless Steel (Type 630) is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and moderate corrosion resistance. High strength is maintained to approximately 600°F (316°C).
General Properties
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
Applications & Standards
| Applications | Standards |
|---|---|
|
|
Chemical Composition
Composition ranges for grade 630 stainless steels:
| Element | Content (%) |
|---|---|
| C | 0.07 max |
| Mn | 1.0 max |
| Si | 1.0 max |
| P | 0.04 max |
| S | 0.030 max |
| Cr | 15.0 - 17.5 |
| Ni | 3.0 - 5.0 |
| Cu | 3.0 - 5.0 |
| Nb+Ta | 0.15 - 0.45 |
Mechanical Properties
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C |
|---|---|---|---|---|
| Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min |
Physical Properties
| Property | Value |
|---|---|
| Density | 7750 kg/m³ |
| Thermal Conductivity at 100°C | 18.4 W/m·K |
| Thermal Conductivity at 500°C | 22.7 W/m·K |
| Specific Heat (0-100°C) | 460 J/kg·K |
| Electrical Resistivity | 800 nΩ·m |
| Mean Coefficient of Thermal Expansion (0-100°C) | 10.8 µm/m·°C |
Corrosion Resistance
Alloy 17-4 PH withstands corrosive attacks better than standard hardenable stainless steels and is comparable to Alloy 304 in most media. For stress corrosion cracking resistance, higher aging temperatures above 1022°F (550°C) are recommended.
Heat Treatment
Solution treatment involves heating to 1040°C for 0.5 hours followed by air cooling. Age hardening at various temperatures achieves different mechanical properties:
| Condition | Hardening Temp (°C) | Time (h) | Typical Hardness HRC | Tensile Strength (MPa) |
|---|---|---|---|---|
| A | Ann | - | 36 | 1100 |
| H900 | 482 | 1 | 44 | - |
| H925 | 496 | 4 | 42 | 1170-1320 |
| H1150 | 621 | 4 | 33 | 930-1080 |
Machining & Welding
Grade 630 stainless steels can be machined in solution-treated condition with rates similar to grade 304. They can be welded using all conventional methods without pre-heating requirements.
Applications
- Engine components
- High strength boat propeller shafts
- Plastic moulding dies
- Valves and gears
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
Location
No.283-1, Youyi Middle Road, Xishan District, Wuxi City, Jiangsu Province
Contact Person
Gao Ben