Grade 17-4PH Stainless Steel Round Bar
Hot rolled stainless steel round bars available in diameters from 8mm to 400mm, ready for immediate delivery from stock inventory.
Product Specifications
| Product | 17-4PH Stainless Steel Round Bar |
|---|---|
| Standard | ASTM, GB, DIN, EN |
| Diameter | 8 - 450mm |
| Length | 6m per piece or custom cutting available |
| Finishing | Black Bar / Bright Bar |
| Main Grades | 201, 301, 303Cu, 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 318, 321, 347, 410, 420, 430, 431, 440a/b/c, 904L, 2205, 2507, Hastelloy C276, C4, C22, Inconel 600, 625, Incoloy 800, 825, 825H, etc. |
| Service | Cutting, surface polishing, heat treatment |
| Brand | Walsin, BAOSTEEL, TISCO, QINGSHAN |
Material Description
17-4PH (Type 630) is a chromium-copper precipitation hardening stainless steel designed for applications requiring high strength and moderate corrosion resistance. This material maintains high strength up to approximately 600°F (316°C).
General Properties
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with copper and niobium additions. This grade combines high strength, hardness (up to 572°F / 300°C), and excellent corrosion resistance. Mechanical properties can be optimized through heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
Applications & Standards
| Applications | Standards |
|---|---|
|
|
Chemical Composition
Composition of 17-4PH Stainless Steel (Grade 630):
| Element | Content (%) |
|---|---|
| C | ≤ 0.07 |
| Mn | ≤ 1.00 |
| Si | ≤ 1.00 |
| P | ≤ 0.04 |
| S | ≤ 0.030 |
| Cr | 15.0 - 17.5 |
| Ni | 3.0 - 5.0 |
| Cu | 3.0 - 5.0 |
| Nb+Ta | 0.15 - 0.45 |
Mechanical Properties
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C (HRC) | Hardness Brinell (HB) |
|---|---|---|---|---|---|
| Solution Treated | 1105 (typ) | 1000 (typ) | 15 (typ) | 38 max | 363 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min | 388 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min | 277 min |
Physical Properties
| Property | Value |
|---|---|
| Density | 7750 kg/m³ |
| Mean Coefficient of Thermal Expansion (0-100°C) | 10.8 µm/m/°C |
| Mean Coefficient of Thermal Expansion (0-315°C) | 11.6 µm/m/°C |
| Thermal Conductivity (at 100°C) | 18.4 W/m·K |
| Thermal Conductivity (at 500°C) | 22.7 W/m·K |
| Specific Heat (0-100°C) | 460 J/kg·K |
| Electrical Resistivity | 800 nΩ·m |
Corrosion Resistance
Grade 630 stainless steel offers superior corrosion resistance compared to standard hardenable stainless steels, performing comparably to Alloy 304 in most media. For optimal resistance to stress corrosion cracking, aging temperatures above 1022°F (550°C) are recommended, with 1094°F (590°C) being ideal for H2S media applications.
Heat Treatment
| Condition | Hardening Temp (°C) | Time (h) | Typical Hardness Rockwell C | Tensile Strength (MPa) |
|---|---|---|---|---|
| A (Annealed) | - | - | 36 | 1100 |
| H900 | 482 | 1 | 44 | - |
| H925 | 496 | 4 | 42 | 1170-1320 |
| H1025 | 552 | 4 | 38 | 1070-1220 |
| H1075 | 580 | 4 | 36 | 1000-1150 |
| H1100 | 593 | 4 | 35 | 970-1120 |
| H1150 | 621 | 4 | 33 | 930-1080 |
Processing Characteristics
Welding
Grade 630 stainless steel can be welded using all conventional methods without requiring pre-heating. Proper design considerations are essential to prevent weldment stresses in high-strength applications.
Machining
This material can be machined in its solution-treated condition, with machining rates comparable to grade 304 stainless steel.
Product Images
Applications
- Engine components
- High-strength boat propeller shafts
- Plastic molding dies
- Valves and gears
- Aerospace components
- Offshore equipment
- Nuclear industry applications
Contact Us
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
Location
No.283-1, Youyi Middle Road, Xishan District, Wuxi City, Jiangsu Province
Contact Person
Gao Ben