17-4PH Precipitation Hardening Stainless Steel Bar with Chromium Nickel Copper and OD 6-300mm
Price:
US $3.42-3.91 / kg
MOQ:
50 kg
Delivery Time:
Negotiable
Product Description
UNS S17400 Precipitation Hardening Stainless Steel Bar
17-4PH stainless steel is a chromium-nickel-copper precipitation hardening martensitic stainless steel designed for applications requiring high strength and moderate corrosion resistance. This material maintains high strength up to approximately 600°F (316°C).
Product Specifications
| Products | 17-4PH Stainless Steel Round Bar |
| Standard | ASTM GB DIN EN |
| Diameter | 8 - 450mm |
| Length | 6m /pcs or cutting as requested |
| Finishing | Black Bar / Bright Bar |
| Service | Cutting, surface polishing, heat treatment |
| Brand | Walsin, BAOSTEEL, TISCO, QINGSHAN |
Material Properties
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with copper and niobium additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
Applications
- Offshore applications (foils, helicopter deck platforms)
- Food industry equipment
- Pulp and paper industry components
- Aerospace (turbine blades)
- Mechanical components
- Nuclear waste casks
Standards
- ASTM A693 grade 630 (AMS 5604B) UNS S17400
- EURONORM 1.4542 X5CrNiCuNb 16-4
- AFNOR Z5 CNU 17-4PH
- DIN 1.4542
Chemical Composition
| Element | Content (%) |
|---|---|
| C | 0.07 max |
| Mn | 1.0 max |
| Si | 1.0 max |
| P | 0.04 max |
| S | 0.030 max |
| Cr | 15.0 - 17.5 |
| Ni | 3.0 - 5.0 |
| Cu | 3.0 - 5.0 |
| Nb+Ta | 0.15 - 0.45 |
Mechanical Properties
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C |
|---|---|---|---|---|
| Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min |
Physical Properties
| Property | Value |
|---|---|
| Density | 7750 kg/m³ |
| Thermal Conductivity at 100°C | 18.4 W/m·K |
| Thermal Conductivity at 500°C | 22.7 W/m·K |
| Specific Heat 0-100°C | 460 J/kg·K |
| Electrical Resistivity | 800 nΩ·m |
Corrosion Resistance
Alloy 17-4 PH withstands corrosive attacks better than standard hardenable stainless steels and is comparable to Alloy 304 in most media. For optimal resistance to stress corrosion cracking, aging temperatures above 1022°F (550°C) are recommended.
Heat Treatment
Solution treatment involves heating to 1040°C for 0.5 hours followed by air cooling. Age hardening at various temperatures achieves the required mechanical properties, with shrinkage varying by condition.
Applications
- Engine components
- High strength and boat propeller shafts
- Plastic moulding dies
- Valves and gears
Product Images
Contact Information
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
Location
No.283-1, Youyi Middle Road, Xishan District, Wuxi City, Jiangsu Province
Contact Person
Gao Ben