Bright Polished 17-4PH Stainless Steel Round Bar Hot Rolled with OD 6-300mm
Price:
US $3.11-3.6 / kg
MOQ:
50 kg
Delivery Time:
Negotiable
Product Description
Bright Polished 17-4PH Stainless Steel Round Bar
High-strength precipitation hardening stainless steel with solid solution finishing, offering excellent mechanical properties and moderate corrosion resistance.
Product Specifications
| Product | 17-4PH Stainless Steel Round Bar |
| Standard | ASTM, GB, DIN, EN |
| Diameter | 8 - 450mm |
| Length | 6m per piece or custom cutting available |
| Finishing | Black Bar / Bright Bar |
| Main Grades | 201, 301, 303Cu, 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 318, 321, 347, 410, 420, 430, 431, 440a/b/c, 904L, 2205, 2507, Hastelloy C276, C4, C22, Inconel 600, 625, Incoloy 800, 825, 825H, etc. |
| Services | Cutting, surface polishing, heat treatment |
| Brand | Walsin, BAOSTEEL, TISCO, QINGSHAN |
Material Description
17-4PH (Type 630) is a chromium-copper precipitation hardening stainless steel designed for applications requiring high strength and moderate corrosion resistance. It maintains high strength up to approximately 600°F (316°C).
General Properties
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with copper and niobium additions. This grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized through heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
Applications & Standards
| Applications | Standards |
|---|---|
|
|
Chemical Composition
Composition of 17-4PH Stainless Steel (Grade 630)
| Element | Content (%) |
|---|---|
| Carbon (C) | max 0.07 |
| Manganese (Mn) | max 1.0 |
| Silicon (Si) | max 1.0 |
| Phosphorus (P) | max 0.04 |
| Sulfur (S) | max 0.030 |
| Chromium (Cr) | 15.0 - 17.5 |
| Nickel (Ni) | 3.0 - 5.0 |
| Copper (Cu) | 3.0 - 5.0 |
| Niobium+Ta (Nb+Ta) | 0.15 - 0.45 |
Mechanical Properties
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C (HRC) | Hardness Brinell (HB) |
|---|---|---|---|---|---|
| Solution Treated | 1105 (typ) | 1000 (typ) | 15 (typ) | 38 max | 363 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min | 388 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min | 277 min |
Physical Properties
| Property | Value |
|---|---|
| Density (kg/m³) | 7750 |
| Mean Coefficient of Thermal Expansion 0-100°C (µm/m/°C) | 10.8 |
| Mean Coefficient of Thermal Expansion 0-315°C (µm/m/°C) | 11.6 |
| Thermal Conductivity at 100°C (W/m·K) | 18.4 |
| Thermal Conductivity at 500°C (W/m·K) | 22.7 |
| Specific Heat 0-100°C (J/kg·K) | 460 |
| Electrical Resistivity (nΩ·m) | 800 |
Applications
- Engine components
- High strength and boat propeller shafts
- Plastic moulding dies
- Valves and gears
Product Images
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
Location
No.283-1, Youyi Middle Road, Xishan District, Wuxi City, Jiangsu Province
Contact Person
Gao Ben