Welding ASTM Hastelloy C Wire Tubing / Plate / Sheet / Pipe Corrosion Resistance
KX Hastelloy C Welding Wire Sheet Pipe Tubing Plate on Hastelloy Alloy
Product Description and Application
Hastelloy C is also known as Hastelloy C, W.N.2.4819
Hastelloy C is nickel-chromium-molybdenum alloy containing tungsten with very low silicon and carbon content. It has excellent corrosion resistance to most corrosive medium in oxidation and reduction states. Excellent resistance to point corrosion, crack corrosion and stress corrosion cracking have been widely used in chemical and petrochemical fields, which is in components and catalytic systems that are exposed to chlorinated organics. This material is especially suitable for high temperature, mixed with impurities of inorganic and organic acids (such as formic acid and acetic acid), seawater corrosion environment. And also suitable for the pulp and paper industry, such as boiling and bleaching containers, scrubbers in FGD systems, reheaters, wet steam fans, equipment and components operating in acid gas environments, reactors for acetic acid and acid products and sulphuric acid condensers
Process Performance and Requirements
- Product Fusion Process
Vacuum Induction Furnace(VIM) and Electroslag Remelting Furnace(ESR)
- Product Chemical Composition
| Cr | Ni | Mo | W | C | Mn | P | S | Fe |
| ≤ | ||||||||
| 14.5-16.5 | Rem | 15.0-17.0 | 3.0-4.5 | 0.08 | 1.00 | 0.040 | 0.030 | 4.0-7.0 |
- Product Physical Property
| Density | ρ=8.9g/cm3 |
| Melting Temperature Range | 1325～1370 ℃ |
- Product Mechanical Property
| Alloy Type |
Tensile Strength Rm N/mm2 |
Yield Strength RP0.2N/mm2 |
Elongation A5 % |
| Hastelloy C | 690 | 310 | 40 |
-
Product Processability
Hot Working
1. The temperature range of hot working is 1200℃ ~ 950℃ and the cooling method is water cooling or rapid air cooling.
2. In order to ensure the best anti-corrosion performance, heat treatment should be carried out after hot working and the workpiece should be directly added to the heat treatment furnace which has been heated up.
Cold Working
1. The work hardening rate is greater than that of austenitic stainless steel, so the processing equipment needs to be selected. The workpiece shall be in solution heat treatment state and shall have intermediate annealing during the cold rolling process
2. If the deformation of cold rolling is greater than 15%, the workpiece needs to be treated with secondary solution.
-
Product Welding Technology
Suitable for welding by any traditional welding process , such as gas tungsten arc welding(GTAW), plasma arc welding, manual subarc welding, metal inert-gas arc welding, melt inert-gas welding(MIG)
- Productive Process
-
Professional Customization
| Cold-drawn Wire | ¢0.3~¢18mm(Delivery in rolls or trays) |
| Hot-Rolling Wire | ¢5.5~¢20mm(Delivery in rolls) |
| Strip | thickness 0.1~4.5*width 6~350mm(Supply in rolls or straight strips) |
| Smooth Forged Rod on a Lathe |
¢60~350mm,L800-2500mm
|
| Hot-rolled Burnishing | ¢20~80mm,L1000-5000mm |
| Cold Drawn and Burnishing | ¢2.5~18mm,L1000-8000mm |
| Seamless Tube | ¢1~275mm,wall thickness 0.2~30,L1000-8000mm |