Gas Pressure Sintering Silicon Nitride Forming Rollers with High Fracture Toughness and Thermal Shock Resistance in Customizable Sizes
Price:
200-500 yuan/kg
MOQ:
Negotiable
Delivery Time:
Negotiable
Brand:
KEGU
Product Description
Gas Pressure Sintering Silicon Nitride Ceramics Si3N4 Forming Rollers
Si3N4 silicon nitride forming rollers are engineered for roll forming machines that manufacture complex variable sections with high profitability. These forming rollers for plastic forming significantly reduce metal adhesion to the rollers, resulting in enhanced product quality.
Gas Pressure Sintering (GPS) Technology
Among the five methods of silicon nitride production, GPSN is the most commonly used for manufacturing Si3N4 components. Gas pressure sintering of silicon nitride occurs at pressures of 1 to 10 MPa and temperatures around 2000°C. The high nitrogen pressure effectively suppresses silicon nitride pyrolysis. This high-temperature sintering process promotes Si3N4 grain growth with minimal sintering aids, producing high-toughness ceramics with long columnar grains and in-situ growth density exceeding 99%. The resulting material offers exceptional toughness, strength, and abrasion resistance, enabling direct production of complex shaped products close to final dimensions, which substantially reduces both production and processing costs.
Silicon Nitride Forming Rollers Specifications
| Size | Customized |
| Color | Black |
| Density | 3.22 g/cm³ |
| Flexural strength | 800 MPa |
| Fracture toughness | 6.5 MPa·m¹/² |
| Thermal stress parameters | 569 K |
Material Properties Data Sheet
| Item | Unit | Si3N4 |
|---|---|---|
| Type | - | Gas pressure sintered |
| Density | g/cm³ | 3.22 |
| Color | - | dark grey |
| Water Absorption | % | 0 |
| Young Modulus | Gpa | 290 |
| Vickers Hardness | Gpa | 18 - 20 |
| Compressive Strength | Mpa | 2200 |
| Flexural Strength | Mpa | 650 |
| Thermal Conductivity | W/m·K | 25 |
| Thermal Shock Resistance | Δ(°C) | 450 - 650 |
| Max. Working Temp. | °C | 1200 |
| Volume Resistivity | Ω·cm | > 10¹⁴ |
| Dielectric Constant | - | 8.20 |
| Dielectric Strength | kV/mm | 16 |
* Tests conducted under room temperature environment
* The above information is offered for comparison only. Exact properties will vary depending on the manufacturing method.
* The above information is offered for comparison only. Exact properties will vary depending on the manufacturing method.
Key Material Characteristics
- High strength over a wide temperature range
- High fracture toughness
- High hardness
- Outstanding wear resistance
- Low thermal expansion and high thermal conductivity
- Good thermal shock resistance
- Good resistance to chemical and oxidation
For detailed specifications, custom requirements, or technical questions, please contact our sales team at sales@industrial-ceramicparts.com.
Packaging and Handling
As ceramic materials, silicon nitride components require careful handling to prevent damage during storage and transportation. Our silicon nitride forming rollers are packaged using suitable outer boxes and protective cushioning materials. Vacuum packing is employed for certain parts to ensure optimal protection and integrity during transit.
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Shaanxi KeGu New Material Technology Co., Ltd
Location
5# Chaoyang Road,Weicheng Sub-district，Qinhan New City, Xixian New Area, Xi'an Shaanxi Province,China,712039
Contact Person
Yuki