KL-1811 Modified Hot Melt Adhesive

KL-1811 Modified Hot Melt Adhesive is a modified hot melt adhesive made from special resins. It can be applied to substrates such as PET, PVC, PU, TPU or PEI. At room temperature, it has a certain initial adhesion force. When subjected to high temperature and pressure, it can be thermally bonded to various materials. It has the advantages of wide application range and strong adhesion.
 

Specification

Product name	KL-1811 Modified Hot Melt Adhesive
Apperanace	Colorless, transparent and viscous liquid
Viscosity	6500-12000cps
Solid content	20-25%
Main chemical components	Special resins, mixed solvents
Features	●High transparency (Does not affect the light transmittance of the substrate, over 93%) ●Resistant to boiling water(Boil at 80 degrees for 2 hours, then boil at 100 degrees for 1 hour) ●High temperature resistance (150 degrees for 30 minutes / 260 degrees for 1 minute) ●Ageing resistant,(double 85 test for 1000 hours) ●No primer adhesion:(Can be rolled up after coating and drying ●Soft: Can be bent at will) ●Excellent powder carrier: can be added with over 70% of flame-retardant powder, magnetic powder, heat-conducting powder, etc.,

Application

Automotive trim

Interior covering: Soft fabric is tightly wrapped around the complex three-dimensional plastic framework through vacuum suction.

Packaging industry

By heating and under vacuum, the plastic sheet is shaped and sealed with the back card.

Display and Touch Control

Bonding various membrane materials. to transparent plastic cover plate ,touch sensor.

Clothing industry

Suitable for adhering to various fabrics such as non-woven fabric, polyester, nylon, cotton fabric, microfiber, nylon, and polyester cloth.

Furniture panel

Permanent bonding of decorative films such as wood grain and stone texture onto the surface of the board, replacing traditional paint or veneer.

Conveyor belt

Bonding unformed nitrile rubber, TPU sheets, nylon sheets, nylon fabric, polyester fabric, PU sheets or unformed PU

Processing

1. Screen printing allows for adjustment of the coating thickness according to actual requirements.
2. This product is activated and bonded by hot pressing at 110-130℃ for 1 minute, then left to cure at 40-50℃ for 24

hours, and will fully crystallize.

Package & Storage

3KG/ can, 15KG /can, 150KG/ barrel

 
Keep the storage area cool and well-ventilated.
Keep the storage container sealed and keep the storage area cool and well-ventilated.
Storage validity period:12 months

Company Profile

Shenzhen Kanglibang Science & Technology Co., Ltd., founded in 2010, is a national high-tech 

enterprise and a designated"Specialized & Sophisticated" Little Giant corporation. With 40,000 m²

production facilities, we pioneer in developing adhesive materials and delivering customized

silicone bonding solutions through integrated R&D,manufacturing, and technical services.

Our technological edge is demonstrated by30+ national patents and the provincial-level
acclaimed "Silicone Pressure-Sensitive Adhesive". The R&D team, composed of seasoned 
experts with decade-long industrial experience, supports strategic partnerships with global
leaders including ABB, Apple,China Aerospace, BYD.

Key credentials:• Certifications: ISO 9001:2015, ISO13485:2016, FDA, LFGB, China Environmental Label 
•RoHS, REACH-compliant production system