Ultra Clear 93% Transmittance Thermoplastic Hot Press Bonding Glue

Price Negotiable

Price: Negotiable

MOQ: 1KG

Delivery Time: 7-12days

Brand: Kanglibang

Product Description

Products Description

With special resins as the core synthetic raw material, KL-17 is a modified hot melt adhesive that can be processed by coating on PET, PVC and PEI. It shows zero initial surface tack at room temperature, produces superior bonding effect under thermal pressing, and is widely applicable with outstanding adhesive toughness.

Application

Specification

Name	KL-17 Hot Melt Adhesive
Appearance	Colorless clear liquid
Main Raw Material	Special resin
Viscosity	500 ± 200 cps
Solid Content	32 ± 3%
Coating thickness	5 μm / 10 μm / 20 μm
Hard drying time	2 min / 4 min / 7 min
Storage condition	0–15℃, avoid heat and direct sunlight

Operating Steps

1. Ensure the substrate surface is clean, dust-free, and oil-free.  
2. Apply/screen print/spray the adhesive onto the substrate. 

3.Bake at 90-110 degrees Celsius for 1-2 minutes to evaporate solvents or moisture. 

4. A: Roll up (with cooling rollers) ☞ Apply release film ☞ For sale/Laminate within 6 months 
B: Lamination: Hot pressing (100-170 degrees Celsius for 1 minute) ☞ Curing (175 degrees Celsius for 40 minutes / 50-60 degrees
Celsius for 24 hours) 

5. After standing for 24 hours, conduct relevant tests.Packing & Delivery