High Quality High Temperature 85-98%  MgO Content Refractory Magnesite Fire Bricks For Industrial Furnace

Refractory Magnesite Fire Bricks are high-temperature, alkaline refractory materials primarily composed of magnesia (MgO) derived from natural magnesite. They are essential in industries requiring extreme thermal and chemical resistance. Their defining characteristic is an exceptionally high melting point (above 2800°C), making them ideal for lining furnaces operating at very high temperatures.

A key performance attribute is their superior resistance to basic (alkaline) slags and corrosive chemical environments, especially those rich in lime and iron oxides. This makes them indispensable in metallurgy for steelmaking furnaces like electric arc furnaces and basic oxygen furnaces, as well as in cement rotary kilns and copper refining.

However, they have notable weaknesses: relatively poor thermal shock resistance (prone to cracking under rapid temperature changes) and lower resistance to acidic slags. To enhance properties, they are often combined with other materials, such as chromium oxide (forming magnesia-chrome bricks) or carbon. Their high refractoriness and chemical stability justify their use despite higher costs and handling considerations.

Common magnesite chrome brick

Direct-Bonded magnesite chrome brick

Advantages:

1.Good performance in high temp refractoriness under load

2.Higher temperate resistant with good refractoriness

3.Lower apparent porosity

4.Lower impurity content

5.Excellent resistance in slag abrasion

6.Higher bulk density

Application:

1.Widely used throughout metallurgical industry

2.Widely used in checker chamber of glass tank, lime kiln, non-ferrous metallurgical furnaces, open heart furnace, iron mixer and EAF of steel-making, and also ferro-alloy furnace, etc.

3.Nonferrous Metal Furnace,PermanentLining For EAF Ladle,Rotary & Shaft Kiln,Reheating Furnace,Various Incinerator