92–98% MgO High Temperature Magnesia Refractory Bricks For Glass Kiln Furnace And Rotary Kiln
Magnesium-chrome bricks are refractory products mainly composed of magnesia (MgO) and chromium oxide (Cr₂O₃), with periclase and spinel as the principal mineral phases. They are manufactured using high-purity sintered magnesia and chromite as the primary raw materials.
To ensure excellent performance, the magnesia used should have the highest possible purity. The chemical composition requirements for chromite are as follows: Cr₂O₃ content of 30–45%, and CaO content not exceeding 1.0–1.5%.
Series:
- Direct bonded Magnesia-Chrome Brick
- Magnesia Chrome Bricks
- Magnesia Zirconia Bricks
- Magnesite Alumina Brick
- Magnesite Alumina Spinel Brick
- Magnesite Brick
- Rebonded Magnesia-Chrome Brick
- Semi Rebonded Magnesia Chrome Brick
Common magnesite chrome brick
| Item | MGe6 | MGe8 | MGe12 | MGe16 |
|---|---|---|---|---|
| MgO % | 80 | 72 | 70 | 65 |
| Cr2O3 % | 7 | 10 | 13 | 17 |
| CaO % | 1.2 | 1.2 | 1.2 | 1.2 |
| SiO2 % | 3.4 | 4 | 4 | 4.2 |
| Al2O3 % | 4.5 | 6.5 | 6 | 6 |
| Fe2O3 % | 4 | 4.8 | 5.5 | 6.5 |
| Apparent Porosity % | 17 | 18 | 18 | 18 |
| Bulk Density g/cm3 | 3 | 3 | 3.02 | 3.05 |
| Cold Crushing Strength Mpa | 55 | 55 | 55 | 50 |
| Refractoriness Under Load °C | 1600 | 1600 | 1600 | 1600 |
Direct-Bonded magnesite chrome brick
| Item | DMGe4 | DMGe8 | DMGe12 | DMGe16 |
|---|---|---|---|---|
| MgO % | 85 | 77 | 74 | 69 |
| Cr2O3 % | 5.5 | 9.1 | 14 | 18 |
| CaO % | 1.1 | 1.4 | 1.2 | 1.2 |
| SiO2 % | 1.3 | 1.2 | 1.2 | 1.5 |
| Al2O3 % | 3.5 | 4 | 3.5 | 4.5 |
| Fe2O3 % | 3 | 6.4 | 5 | 5.7 |
| Apparent Porosity % | 18 | 18 | 18 | 18 |
| Bulk Density g/cm3 | 3.02 | 3.04 | 3.06 | 3.08 |
| Cold Crushing Strength Mpa | 50 | 50 | 55 | 55 |
| Refractoriness Under Load °C | 1700 | 1700 | 1700 | 1700 |
| Thermal expansion % 1000°C |
1 | 1 | 1 | 0.9 |
| Thermal expansion % 1600°C |
1.8 | 1.8 | 1.8 | 1.6 |
Key Features
- Excellent high-temperature resistance
- Strong refractoriness under load
- Superior slag corrosion and abrasion resistance
- High density with low porosity
- Low impurity content
Main Applications
- Non-ferrous metal furnaces
- Rotary & shaft kilns
- Incinerators
- Reheating furnaces
- EAF ladle permanent lining
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Qingdao Leadsun Refractory Co., Ltd
Location
No. 700, Qingshan Road, Licang District, Qingdao, China
Contact Person
Tony