Product Description
Product Overview
This specification sheet details the 0603 (X6S) surface mount ceramic capacitor (MLCC) designed for high-voltage electronic circuits. It is suitable for applications such as coupling, filtering, and resonance in switching power supplies, AC-DC and DC-DC converters, network/communication interfaces, LCD module backlight power supplies, and energy-saving lamp ballasts. The capacitors are manufactured with a multi-layer ceramic structure, featuring internal electrodes, external electrodes, a nickel layer, and a tin layer.
Product Attributes
- Temperature Characteristics: X6S (22%)
- Termination Material: Copper/Silver-Nickel-Tin (from inside to outside)
- Compliance: RoHS Directive, REACH Regulation (SVHC)
Technical Specifications
| Item | Specification | Test Method |
|---|---|---|
| Application Range | High-voltage electronic circuits for coupling, filtering, resonance. Applications include switching power supplies, AC-DC converters, DC-DC converters, network/communication interfaces, LCD module backlight power supplies, and energy-saving lamp ballasts. | - |
| Standard Conditions | Ambient Temperature: 15~35 Ambient Humidity: 45~75%RH Ambient Pressure: 86~106kPa | - |
| Standard Relative Conditions | Ambient Temperature: 252 Ambient Humidity: 60~70%RH Ambient Pressure: 86~106kPa | - |
| Product Name Composition | Example: 0603 X6S 105 K 160 N T Product Size Code Temperature Characteristic Nominal Capacitance Capacitance Tolerance Rated Voltage (DC) Termination Material Packaging Method | - |
| Product Structure | Ceramic Dielectric Internal Electrode External Electrode Nickel Layer Tin Layer | - |
| Product Dimensions (0603) | Model: 0603 (1608) Dimensions (mm): L: 1.600.15, W: 0.800.15, T: 0.800.15, WB: 0.300.10 | Vernier Caliper Measurement |
| Operating Temperature Range | -55~+105 | - |
| Appearance and Dimensions | 1. No visible damage. 2. Dimensions meet specifications. | Visual inspection; Vernier caliper measurement. |
| Capacitance | Within specified tolerance. (See Note 1 for initial value measurement) | Frequency and voltage as per NPO or X7R/X5R/X6S/X7S/Y5V characteristics. |
| Dissipation Factor (DF Value) | X6S characteristics: See Note 1. | Frequency and voltage as per X7R/X5R/X6S/X7S/Y5V characteristics. |
| Insulation Resistance (IR) | X6S characteristics: IR 10000M, C 25nF; IR*C 100S, C > 25nF. | Test voltage: 500V DC or rated voltage (whichever is lower). Test time: 605 sec. Humidity: 75%. Temperature: 255. |
| Dielectric Withstanding Voltage (DC) | No dielectric breakdown or damage. Test voltage is 1.5 to 2.5 times rated voltage depending on Ur. | Voltage applied for 2 sec. Ramp time: 1-10 sec. |
| Solderability | Tinning rate > 90%. No visible damage. | Preheat 80-120 for 10-30 sec. Lead-free solder, flux. Solder temp: 2455. Soldering time: 20.5 sec. |
| Solder Heat Resistance | No visible damage, tinning rate 90%. Capacitance change rate for X6S: |C/C| 22%. DF value and IR as per initial standard. | Preheat 100-200 for 102 sec. Immersion temp: 2605. Immersion time: 51 sec. Conditioned at room temp for 242 hours. |
| Bending Strength | No visible damage. Capacitance change rate: |C/C| 10%. | Test substrate (Al2O3 or PCB) bent to 1mm depth at 0.5mm/sec. Measurement in bent state. |
| Terminal Pull Strength | No visible damage. | - |
| Temperature Cycling | Capacitance change rate for X6S: |C/C| 10%. | 5 cycles of temperature extremes (-55 to +105). Conditioned at room temp/humidity for 242 hours before testing. |
| Damp Heat Resistance | No visible damage. Capacitance change rate for X6S: |C/C| 10%. DF value 2x initial standard. IR for X6S: IR 1000M or IR*C 25S (whichever is smaller). | 402, 90-95%RH for 50024 hours. Conditioned at room temp/humidity for 24 hours after test. |
| High Temperature Load Test | No visible damage. Capacitance change rate for X6S: |C/C| 20%. DF value 2x initial standard. IR for X6S: IR 2000M or IR*C 50S (whichever is smaller). | 853 for 100048 hours. Voltage applied is 1.5 to 2 times rated voltage depending on Ur. Charge/discharge current limited to 50mA. Conditioned at room temp/humidity for 484 hours after test. |
| Circuit Board Bending Test | No cracks or defects. | Capacitor soldered onto fixture, then subjected to bending force. |
| Packaging (Tape & Reel) | 0603: 4000 pcs 0805: 3000 pcs (T1.35mm) 1206: 3000 pcs (T1.60mm) 1210: 2000 pcs (T1.85mm) 1808: 1000 pcs (T1.85mm) 1812: 800 pcs (T1.85mm) | - |
Note 1: Initial value measurement for capacitance, DF, and IR requires preheating at 150 for 1 hour, followed by 48 hours at room temperature and standard pressure.
Note 2: DF values for X7R/X5R/X6S/X7S/Y5V characteristics are detailed in a separate table (Page 6).
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Beijing Silk Road Enterprise Management Services Co., Ltd.
Location
16 Floor, Unit B, Jiatai International Mansion, No 41, Dongsihuan Zhong Road, Chaoyang District, Beijing
Contact Person
Sellina