High voltage chip ceramic capacitor AIDE CAPACITOR 0805X6S106K160NT compliant with RoHS and REACH regulations
Price:
Negotiable
MOQ:
Negotiable
Delivery Time:
Negotiable
Product Description
Product Overview
This specification sheet details 0805(X6S) chip ceramic capacitors designed for high-voltage electronic circuits. They are suitable for coupling, filtering, and resonant applications, commonly found in switching power supplies, AC-DC and DC-DC converters, network/communication interfaces, LCD module backlight power supplies, and energy-saving lamp ballasts. These high-voltage MLCCs offer reliable performance across various demanding electronic systems.
Product Attributes
- Temperature Characteristics: X6S (22%)
- Termination Material: Copper/Silver-Nickel-Tin (from inside to outside)
- Environmental Compliance: RoHS Directive, REACH Regulation (SVHC)
Technical Specifications
| Item | Specification | Test Method |
|---|---|---|
| Application Range | High-voltage electronic circuits for coupling, filtering, resonance. Applications include switching power supplies, AC-DC converters, DC-DC converters, network/communication interfaces, LCD module backlight power supplies, energy-saving lamp ballasts. | - |
| Standard Conditions | Ambient Temperature: 15~35 Ambient Humidity: 45~75%RH Ambient Pressure: 86~106kPa | - |
| Standard Relative Conditions | Ambient Temperature: 252 Ambient Humidity: 60~70%RH Ambient Pressure: 86~106kPa | - |
| Product Structure & Dimensions | Structure: Ceramic Dielectric, Internal Electrode, External Electrode, Nickel Layer, Tin Layer. Dimensions (0805/2012): L: 2.000.20mm, W: 1.250.20mm, T: 0.800.20mm, WB: 1.000.20mm | Visual inspection for appearance; Vernier caliper for dimensions. |
| Operating Temperature Range | -55~+105 | - |
| Appearance & Dimensions | 1. No visible damage. 2. Dimensions meet specifications. | Visual inspection; Vernier caliper measurement. |
| Capacitance | Within specified tolerance. | NPO: 1000pF @ 1MHz10%, 1.00.2Vrms; >1000pF @ 1KHz10%, 1.00.2Vrms. X7R/X7T/X5R: 10uF @ 1KHz10%, 1.00.2Vrms; >10uF @ 120Hz24, 0.50.1Vrms. |
| Dissipation Factor (DF Value) | NPO: DF0.56% (Cr5pF); DF1.5[(150/Cr)+7]10-4 (5pFCr50pF); DF0.15% (50pFCr). Measured at 110%MHz, 1V0.2rms for Cr1000pF; 110%KHz, 1V0.2rms for Cr1000pF. X7R/X5R/X6S/X7S/Y5V: See Note 1. Measured at 110%KHz, 1V0.1rms for Cr10uF; 12024Hz, 0.5V0.1rms for Cr10uF. | - |
| Insulation Resistance (IR) | NPO: IR50000M (C10nF); IR*Cr500S (C10nF). Test Voltage: 500V (Rated voltage 500V) or Rated voltage (Rated voltage 500V). Test time: 605 sec. Humidity: 75%. Temperature: 255. Charge/discharge current: 50mA. X7R/X6S/X5R: IR10000M (C25nF); IR*Cr100S (C25nF). | - |
| Dielectric Strength (DC) | No dielectric breakdown or damage. Test voltage is a multiple of rated voltage (Ur): 2.5x (Ur=100V), 2.0x (Ur=200V/250V), 1.5x (Ur=450/500/630V), 1.2x (1KVUr2KV), 1.1x (Ur2KV). Ramp time: 1-10S. Hold time: 2S. | - |
| Solderability | Soldering rate >90%. No visible damage. Preheating: 80-120 for 10-30 sec. Lead-free solder, flux used. Solder temperature: 2455. Soldering time: 20.5 sec. | - |
| Solder Heat Resistance | Appearance: No visible damage, soldering rate 90%. Preheating: 100-200 for 102 sec. Immersion temperature: 2605. Immersion time: 51 sec. Clean with solvent. Store at room temperature for 242 hours. Capacitance Change Rate: NPO: |C/C|0.5% or 0.5pF (whichever is greater). X7R: |C/C|15%. X7T: -33% C/C22%. X6S: |C/C|22%. DF Value: As per No. 4. IR: As per No. 5. | - |
| Bending Strength | No visible damage. Test substrate: Al2O3 or PCB (1.6mm thickness, 100mm length, 40mm width). Bending depth: 1mm. Pressing speed: 0.5mm/sec. Capacitance Change Rate: |C/C|10%. | - |
| Terminal Connection Strength | No visible damage. | - |
| Temperature Cycling | NPO: |C/C|2.5% or 0.25pF (whichever is greater). X7R/X5R: |C/C|7.5%. X6S: |C/C|10%. Pre-treatment (X7R): 1 hour at upper temp, 241 hours at ambient. 5 cycles. Post-test: 242 hours at ambient conditions. Steps: Lower temp (303 min), Ambient (2-3 min), Upper temp (303 min), Ambient (2-3 min). | - |
| Damp Heat Resistance | Appearance: No visible damage. Post-test: 24 hours at ambient conditions. Temperature: 402 Humidity: 90~95%RH Time: 50024 hours. Capacitance Change Rate: NPO: |C/C|2% or 1pF (whichever is greater). X7R/X6S/X5R: |C/C|10%. DF Value: 2x initial standard. IR: NPO: IR2500M or IR*Cr25S (whichever is smaller). X7R/X6S/X5R: IR1000M or IR*Cr25S (whichever is smaller). | - |
| High Temperature Load Test | Appearance: No visible damage. Charge/discharge current: 50mA. Post-test: 484 hours at ambient conditions. Temperature: 853 Time: 100048 hours. Voltage: 2x rated voltage (100VV250V), 1.5x rated voltage (250VV1KV), 1.2x rated voltage (1KVV). Capacitance Change Rate: NPO: |C/C|2% or 1pF (whichever is greater). X7R/X6S/X5R: |C/C|20%. DF Value: 2x initial standard. IR: NPO: IR4000M or IR*Cr40S (whichever is smaller). X7R/X6S/X5R: IR2000M or IR*Cr50S (whichever is smaller). | - |
| Circuit Board Bending Performance | No cracks or other defects. Soldering via reflow. | - |
| Packaging (Tape & Reel) | 0805 (2012): 3000 pcs (T1.35mm), 3000 pcs (T1.35mm) 1206 (3216): 2000 pcs (T1.60mm), 3000 pcs (T1.60mm) 1210 (3225): 2000 pcs (T1.85mm), 1000 pcs (T1.85mm) 1808 (4520): 800 pcs 1812 (4532): 500 pcs | - |
| Packaging (Paper Tape) | 1005 (0402): 4000 pcs 0603: 4000 pcs 0805: 4000 pcs | - |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Beijing Silk Road Enterprise Management Services Co., Ltd.
Location
16 Floor, Unit B, Jiatai International Mansion, No 41, Dongsihuan Zhong Road, Chaoyang District, Beijing
Contact Person
Sellina