AIDE CAPACITOR 0805C0G330J251NT high voltage MLCC capacitor for energy saving lamps and networking power supplies
Price:
Negotiable
MOQ:
Negotiable
Delivery Time:
Negotiable
Product Description
Product Description
Medium and High voltage MLCCs designed for coupling, wave filtering, and resonant applications in high voltage circuits. Suitable for switch power supplies, AC-DC and DC-DC power chargers, networking/communication interfaces, LCD backlight unit power supplies, and energy-saving lamps.
Product Attributes
- Material: Ceramic dielectric, Inner electrode, Outer electrode, Nickle layer, Tin layer
- Terminal composition: Au/Ag-Ni-Sn
- Packing: Tape/Reel (T), Bag packing (P)
Technical Specifications
| Item | Specification/Requirement | Testing Method |
|---|---|---|
| Temperature Characteristic | C0G (0±30 PPM/°C), X7R (±15%), X5R (±15%) | |
| Nominal Electrostatic Capacity | 8R0=8.0pF, 100=10pF, 101=100pF | |
| Tolerance of Electrostatic Capacity | B:±0.1pF, C:±0.25pF, D:±0.5pF, F:±1%, G: ±2%, J: ±5%, K: ±10%, M: ±20%, Z:+80%/-20% | |
| Rated Voltage (DC) | 250V, 251=250V, 252=2500V | |
| Temperature Range | -55~+125°C | |
| Static Capacity (NPO) | ≤1000pF: 1MHz±10%, 1.0±0.2Vrms >1000pF: 1KHz±10%, 1.0±0.2Vrms | |
| Static Capacity (X7R/X7T/X7P) | ≤10uF: 1KHz±10%, 1.0±0.2Vrms >10uF: 120Hz±24, 0.5±0.1Vrms | |
| Dissipation Factor (DF) (NPO) | DF≤0.56 (Cr<5pF) DF≤1.5[(150/Cr)+7]×10-4 (5pF≤Cr<50pF) DF≤0.15% (50pF≤Cr) | Cr≤1000pF, 1±10%MHz, 1V±0.2rms Cr>1000pF, 1±10%KHz, 1V±0.2rms |
| Dissipation Factor (DF) (X7R/X7T/X7P) | See Note 1 | Cr≤10uF, 1±10%KHz, 1V±0.1rms Cr>10uF, 120±24Hz, 0.5V±0.1rms |
| Insulation Resistance (IR) (NPO) | IR≥50000MΩ, C≤10nF IR*Cr≥500S, C>10nF | Rated voltage, Time:60±5s, Humidity:≤75%, Temp:25±5°C, Current:≤50mA |
| Insulation Resistance (IR) (X7R/X7T/X7P) | IR≥10000MΩ, C≤25nF IR*Cr≥100S, C>25nF | Rated voltage, Time:60±5s, Humidity:≤75%, Temp:25±5°C, Current:≤50mA |
| Hi-pot (DC) | No dielectric breakdown or damage | Voltage Raising time:110S, Voltage maintaining time2S |
| Solderability | Soldering area≥90% | Pre-heating 80-120, 10-30s; Solder temp 245±5, Solder time 2±0.5s |
| Resistance to the heat of soldering | No damage, soldering area≥90% | Pre-heating 100-200, 10±2s; Solder temp 265±5, Solder time 5±1s |
| Electrostatic Capacity Change Rate (after Soldering) | NPO: ¦ΔC/C¦≤0.5% or ±0.5pF X7R: ¦ΔC/C¦≤15% X7T: -33% ≤ΔC/C≤22% X7P: ¦ΔC/C¦≤10% | Pre-heating 150 1hour, then place 48hours under normal pressure & temperature. |
| Flexural Strength | No damage | Base board: Al2O3 /PCB, PCB thickness: 1.6mm, Length: 100mm, Width: 40mm, Flexural depth: 1mm, Bend speed: 0.5mm/sec. |
| Electro static capacity change rate (Flexural) | ¦ΔC/C¦≤10% | Test it under the flexural status. |
| Terminal bonding strength | No visual damage | Applied Force: 5N, Duration: 10±1S |
| Thermal Shock | NPO: ¦ΔC/C¦≤2.5% or 0.25pF X7R/X7P: ¦ΔC/C¦≤0.5% X7T: ¦ΔC/C¦≤10% | Pre-condition(X7R h characteristic):Upper limit temp 1hour, place 24±1 hours. Run 5 cycles. Test after place 24±2 hours normal temp & humidity. |
| Temperature Moisture Exposure | Visual: No visual damage Capacity Change Rate: NPO: ¦ΔC/C¦≤2% or 1pF X7R/X7T/X7P: ¦ΔC/C¦≤10% DF: ≤2 times initial standard IR: NPO: IR≥2500MΩ or IR*Cr≥25S X7R/X7T/X7P: IR≥1000MΩ or IR*Cr≥25S | Temp: 40±2°C, Humidity: 90~95%RH, Time: 500±+24 hours. Test after place 24±2 hours normal temp & humidity. |
| High Temperature Exposure | Visual: No visual damage Capacity Change Rate: NPO: ¦ΔC/C¦≤2% or 1pF X7R/X7T/X7P: ¦ΔC/C¦≤20% DF: ≤2 X initial standard IR: NPO: IR≥4000MΩ or IR*Cr≥40S X7R/X7T/X7P: IR≥2000MΩ or IR*Cr≥50S | Temp: 125±3°C, Time: 1000±48 hours. Voltage: 100V≤V≤250V (2x Rated voltage), 250V<V<1KV (1.5x rated voltage), 1KV≤V (1.2x rated voltage). Test after place 48 hours under normal pressure & temperature. |
| PCB Flexural Strength | No crack and other defect | Soldering the MLCC on the PCB, then pressing direction based on the photo. |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Beijing Silk Road Enterprise Management Services Co., Ltd.
Location
16 Floor, Unit B, Jiatai International Mansion, No 41, Dongsihuan Zhong Road, Chaoyang District, Beijing
Contact Person
Sellina