Compact 0603 size multilayer ceramic capacitor CGA0603X7R224K250JT 220nF capacitance 25Vdc rated voltage

Price Negotiable

Price: Negotiable

MOQ: Negotiable

Delivery Time: Negotiable

Product Description

Product Overview

The CGA0603X7R224K250JT is a multilayer ceramic capacitor (MLCC) with X7R temperature characteristics, a capacitance of 220nF, and a rated voltage of 25Vdc. It is designed for various electronic applications and features a compact 0603 size. This product specification outlines the parameters, dimensions, electrical characteristics, and testing methods for this capacitor.

Product Attributes

Brand: Not specified
Origin: Not specified
Material: Dielectric Ceramic, Nickel Inner Electrode, Copper Outer Electrode
Color: Not specified
Certifications: JIS C 5101, IEC60384 (Reference Standards for Testing)

Technical Specifications

Item	Specification	Test Method (Reference Standard: JIS C 5101, IEC60384)
Model	CGA0603X7R224K250JT	-
Dimensions (mm)	Length: 1.600.20, Width: 0.800.20, Thickness: 0.800.20	Micrometer measurement
Capacitance	220nF 10%	25, 1.00.1 KHz, 1.00.2Vrms
Rated Voltage	25Vdc	-
Temperature Characteristic	X7R (15% within -55 to +125)	Measured at specified temperature stages after thermal equilibrium
Dielectric Ceramic	X7R	-55~+125, 15% capacitance change
Inner Electrode	Nickel	-
Outer Electrode	Copper	-
Packaging	Tape & Reel (180mm)	4,000 pcs/reel
Appearance	No defects or abnormalities	Visual (microscope) inspection
Voltage Proof	250% RV (for RV50V)	1 to 5 seconds, Max 50mA charge/discharge current
Insulation Resistance (I.R.)	100M (for X7R/X5R)	25, Max 50mA charge/discharge current, 1 minute charge time
Quality Factor/Dissipation Factor (D.F.)	10F: 3.5% (C103), 5.0% (104C>103), 10% (104>C106)	120Hz24Hz, 0.5V0.1Vrms (for C10F); 1.00.1 KHz, 1.00.2Vrms (for C>10F)
Adhesive Strength of Termination	No terminal detachment, ceramic breakage	5 N force, 101 sec application time
Substrate Bending Test	Appearance: No defects or abnormalities; C/C	Bending 1 mm
Solderability	95% of terminals should be uniformly and continuously soldered	Sn-3.0Ag-0.5 Cu solder, 2455C, 20.5s dwell time
Resistance to Soldering Heat	Appearance: No cracks; Capacitance change: 7.5% (X7R/X5R); DF/Q: Same as initial; I.R.: Same as initial; Voltage Proof: No defects	2605C solder bath, 101s test time
Temperature Cycle	Appearance: No defects or abnormalities; Capacitance change: 7.5% (X7R/X5R); DF/Q: Same as initial; I.R.: Same as initial	5 cycles, -55 to +125
High Temperature High Humidity (Load)	Appearance: No defects or abnormalities; Capacitance change: 12.5% (X5R/X7R); DF/Q: 7% or 2x initial (16V), 5% or 2x initial (25V); I.R.: 500M or R.C5s	402, 90%-95% RH, 50024 hours, Rated voltage
Life Test	Appearance: No defects or abnormalities; Capacitance change: 12.5% (X5R/X7R); DF/Q: 7% or 2x initial (16V), 5% or 2x initial (25V); I.R.: 1G or R.C50s	Highest operating temp 3, 100012 hours, 100% R.V.