Multilayer Ceramic Chip Capacitors IHHEC C1206N220J050T with 500V Rated Voltage and RoHS Compliance
Price:
Negotiable
MOQ:
Negotiable
Delivery Time:
Negotiable
Product Description
Multilayer Ceramic Chip Capacitors HVC-008-0807
This specification applies to Multilayer Ceramic Chip Capacitors (MLCC) designed for use in electric equipment with voltage ratings from 100V to 5KV. These MLCCs support Lead-Free wave and reflow soldering, maintaining their electrical characteristics and reliability. This product is compliant with RoHS.
Product Attributes
- Brand: HVC
- Certifications: RoHS compliant
Technical Specifications
| Part Number Code | Product Code | Chip Size | Temperature Characteristics | Capacitance Unit | Nominal Capacitance | Capacitance Tolerance | Rated Voltage | Tapping Code |
| C0805X472K501T | C (MLCC) | 0805 (2.001.25 mm) | X7R (15% @ -55~+125) | pF | 472 (4,700.0 pF) | K (10.0%) | 501 (500Vdc) | T (Tape & Reel) |
Performance
| No. | Item | Specification | Test Condition |
| 1 | Visual | No abnormal exterior appearance | Visual inspection |
| 2 | Dimension | See Page 3 | Visual inspection |
| 3 | Insulation Resistance | 10,000M or 500/C (Whichever is Smaller) | V500V, Rated Voltage; V500V, Applied 500Vdc; Charge Time60sec. |
| 4 | Capacitance | Within The Specified Tolerance | Class (NPO/SL); Class (X7R/X5R/X7E/Y5V/Z5U/Y5U) |
| 5 | Tan | Class (NPO/SL): More Than 30pF: Q1000; 30pF & Below: Q400 (+20C) Char. Maximum X7R: 2.5%; Class (Z5U/Y5U): 4.0% | C-Meter |
| 6 | Withstanding Voltage | No dielectric breakdown or mechanical breakdown | Char. Temp. Range Cap. Change(%) NPO: 30 ppm/; SL: +350~-1000ppm; X7R: 15%; Y5U: +22% ~-56%; Z5U: +22% ~-56% |
| 7 | Temperature Capacitance Coefficient | Class [C2-C1/C1(T2-T1)] 100%; Class (C2-C1)/C1 100% | T1: 25; T2: Test temperature; C1: Capacitance at 25; C2: Capacitance at T2 |
| 8 | Adhesive Strength of Termination | No indication of peeling shall occur on the terminal electrode. A 5Nf (0.5Kgf) pull force shall be applied for 101 second. Appearance: No mechanical damage. | |
| 9 | Resistance to Flexure of Substrate | Capacitance Change: NPO/SL: 5.0%; X7R: 12.5%; Y5U/Z5U: 30.0% | Bending shall be applied to the 1.0 mm with 1.0 mm/sec. |
| 10 | Solderability | More than 90% of the terminal surface is to be soldered newly, so metal part does not come out or dissolve. Appearance: No mechanical damage. | Solder Temp: 2455; Dip Time: 50.5 sec; Immersing Speed: 2510% mm/s; Solder: H63A; Flux: Rosin; Preheat: 80~120 for 10~30sec. |
| 11 | Resistance To Soldering Heat | Capacitance Change: Class (NPO/SL): Within 2.5% or 0.25pF (whichever is larger); X7R: Within 10%; Class (Z5U/Y5U): Within 20% | Preheat: 15010 for 60~120sec; Dip: Solder Temp. 2605; Dip Time: 101sec; Immersing Speed: 2510% mm/s; Solder: H63A; Flux: Rosin. Measure after cooling. |
| 12 | Temperature Cycle | Capacitance Change: Class (NPO/SL): Within 5.0% or 0.5pF (whichever is larger); X7R: Within 15%; Class (Z5U/Y5U): Within 30% | Capacitor shall be subjected to five cycles of the temperature cycle as following: Step 1: Min Rated Temp. (+0/-3) 30 min; Step 2: 25 3 min; Step 3: Max Rated Temp. (+3/-0) 30 min; Step 4: 25 3 min. Solder the capacitor on P.C. board before testing. |
| 13 | Humidity | Capacitance Change: Class (NPO/SL): Within 3.0% or 0.3pF (whichever is larger); X7R: Within 15%; Class (Z5U/Y5U): Within 30% | Temperature: 402; Relative Humidity: 90~95%RH; Test Time: 500+12/-0Hr. Solder the capacitor on P.C. board before testing. |
| 14 | High Temperature Load (Life Test) | Capacitance Change: Class (NPO/SL): Within 2.5% or 0.25pF (whichever is larger); X7R: Within 7.5%; Class (Z5U/Y5U): Within 20% | Temperature: Max operation temperature; Test Time: 1000+12/-0Hr; Applied DC voltage (following table). Current Applied: 50 mA Max. |
| 15 | Vibration | Insulation Resistance: To satisfy the specified initial value. | Vibrate with amplitude of 1.5mm P-P changing frequencies from 10Hz to 55Hz and back to 10Hz in about 1 min. Repeat for 2 hours each in 3 perpendicular directions. Solder the capacitor on P.C. Board before testing. |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Beijing Silk Road Enterprise Management Services Co., Ltd.
Location
16 Floor, Unit B, Jiatai International Mansion, No 41, Dongsihuan Zhong Road, Chaoyang District, Beijing
Contact Person
Sellina