Multilayer Ceramic Chip Capacitors with 100V to 5KV Voltage Range IHHEC C1206N151J202T RoHS Compliant
Price:
Negotiable
MOQ:
Negotiable
Delivery Time:
Negotiable
Product Description
MULTILAYER CERAMIC CHIP CAPACITORS HVC-008-0807
This specification applies to Multilayer Ceramic Chip Capacitors (MLCC) designed for electric equipment with a voltage range of 100V to 5KV. These MLCCs support Lead-Free wave and reflow soldering, maintaining their electrical characteristics and reliability. This product is compliant with RoHS.
Product Attributes
- Brand: HVC
- Certifications: RoHS compliant
Technical Specifications
| Part Number Code | Product Code | Chip Size Code | Temperature Characteristics Code | Capacitance Unit | Nominal Capacitance | Capacitance Tolerance Code | Rated Voltage Code | Tapping Code |
|---|---|---|---|---|---|---|---|---|
| C0805X472K501T | C (Multilayer Ceramic Chip Capacitor) | 0805 (2.00x1.25 mm) | X7R (15% over -55~+125) | pF | 472 (4,700.0 pF) | K (10.0%) | 501 (500Vdc) | T (Tape & Reel) |
| Chip Size Code | Length (mm) | Width (mm) | Thickness (mm) | Termination Width (min) (mm) |
|---|---|---|---|---|
| 0805 | 2.000.20 | 1.250.20 | 0.850.10 | 0.20 |
| Item | Specification | Test Condition |
|---|---|---|
| Visual | No abnormal exterior appearance | Visual inspection |
| Dimension | See Page 3 | Visual inspection |
| Insulation Resistance | 10,000M or 500/C (whichever is smaller) | V500V, Rated Voltage; V500V, Applied 500Vdc; Charge Time: 60sec. |
| Capacitance | Within The Specified Tolerance | Class NPO/SL; Class |
| Tan | Class NPO/SL: More Than 30pF: Q 1000; 30pF & Below: Q 400; Class X7R: 2.5%; Z5U/Y5U: 4.0% | Q Class : +20C (C : Capacitance, pF); Char. Maximum X7R: 2.5%; Tan Class : Z5U/Y5U: 4.0% |
| Withstanding Voltage | No dielectric breakdown or mechanical breakdown | Temp. Range: NPO -55~+125, SL -30~+85, X7R -55~+125, Y5U -30~+85, Z5U +10~+85; V500V: 200% Rated Voltage; 500VV1000V: 150% Rated Voltage; 1000V: 120% Rated Voltage for 1~5 sec. |
| Temperature Capacitance Coefficient | Class : NPO 30 ppm/, SL +350~-1000ppm; Class : X7R 15%, Y5U +22%~-56%, Z5U +22%~-56% | Class : [C2-C1/C1(T2-T1)] 100%; Class : (C2-C1)/C1 100%; T1: 25; T2: Test temperature; C1: Capacitance at 25; C2: Capacitance at T2 |
| Adhesive Strength of Termination | No indication of peeling, no mechanical damage | A 5Nf (0.5Kgf) pull force for 101 sec. |
| Resistance to Flexure of Substrate | Capacitance Change: NPO/SL 5.0%, X7R 12.5%, Y5U/Z5U 30.0% | Bending applied to 1.0 mm at 1.0 mm/sec. |
| Solderability | More than 90% of terminal surface newly soldered, no metal part comes out or dissolves, no mechanical damage | Solder Temp: 2455; Dip Time: 50.5 sec; Immersing Speed: 2510% mm/s; Solder: H63A; Flux: Rosin; Preheat: 80~120 for 10~30sec. |
| Resistance To Soldering Heat | Capacitance Change: Class (NPO/SL) Within 2.5% or 0.25pF (whichever is larger); X7R Within 10%; Class Z5U/Y5U Within 20%. Other specs to satisfy initial values. | Preheat: 15010 for 60~120sec; Dip: Solder Temp 2605; Dip Time: 101sec; Immersing Speed: 2510% mm/s; Solder: H63A; Flux: Rosin. Measure after cooling. |
| Temperature Cycle | Capacitance Change: Class (NPO/SL) Within 5.0% or 0.5pF (whichever is larger); X7R Within 15%; Class Z5U/Y5U Within 30%. Other specs to satisfy initial values. | Subject to five cycles of specified temperature steps. Solder on P.C. board before testing. Measure after cooling. |
| Humidity | Capacitance Change: Class (NPO/SL) Within 3.0% or 0.3pF (whichever is larger); X7R Within 15%; Class Z5U/Y5U Within 30%. Other specs to satisfy initial values. | Temp: 402; Relative Humidity: 90~95%RH; Test Time: 500+12/-0Hr. Solder on P.C. board before testing. Measure after cooling. |
| High Temperature Load (Life Test) | Capacitance Change: Class (NPO/SL) Within 2.5% or 0.25pF (whichever is larger); X7R Within 7.5%; Class Z5U/Y5U Within 20%. Other specs to satisfy initial values. | Applied DC voltage (following table) at max operation temp 3 for 1hr, then set for 484 hrs at room temp. Test Time: 1000+12/-0Hr. Measure after cooling. |
| Vibration | Insulation Resistance: To satisfy the specified initial value. | Solder on P.C. Board before testing. Vibrate with amplitude of 1.5mm P-P from 10Hz to 55Hz and back to 10Hz in ~1 min. Repeat for 2 hours each in 3 perpendicular directions. |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Beijing Silk Road Enterprise Management Services Co., Ltd.
Location
16 Floor, Unit B, Jiatai International Mansion, No 41, Dongsihuan Zhong Road, Chaoyang District, Beijing
Contact Person
Sellina