Product Overview

The MGFL series of multilayer chip ferrite large current inductors are designed for various electronic applications requiring efficient current handling and inductance. These inductors are manufactured by SHENZHEN MICROGATE TECHNOLOGY CO., LTD and are compliant with RoHS standards.

Product Attributes

Brand: MICROGATE
Origin: Shenzhen, China
Material: Ferrite (Ni-Cu-Zn series), Silver (Ag), Nickel-Tin (Ni-Sn)
Certifications: RoHS compliant

Technical Specifications

Customer Part No.	Microgate Part No.	Inductance (H)	Tolerance	Test Freq. (MHz)	SRF (MHz) min	RDC () max	IR* (mA) max	Dimensions (mm) L	Dimensions (mm) W	Dimensions (mm) T	Dimensions (mm) a1, a2
	MGFL1608F1R0MT-LF	1.0	20%	1	125	0.18	1000	1.600.15	0.800.15	0.800.15	0.300.20
	MGFL1608F1R5MT-LF	1.5	20%	1	109	0.22	800	1.600.15	0.800.15	0.800.15	0.300.20
	MGFL1608F2R2MT-LF	2.2	20%	1	90	0.30	700	1.600.15	0.800.15	0.800.15	0.300.20
	MGFL1608F3R3MT-LF	3.3	20%	1	70	0.40	600	1.600.15	0.800.15	0.800.15	0.300.20
	MGFL1608F4R7MT-LF	4.7	20%	1	50	0.50	500	1.600.15	0.800.15	0.800.15	0.300.20
	MGFL1608F100MT-LF	10	20%	1	33	0.80	400	1.600.15	0.800.15	0.800.15	0.300.20
	MGFL1608F150MT-LF	15	20%	1	20	0.90	220	1.600.15	0.800.15	0.800.15	0.300.20
	MGFL1608F220MT-LF	22	20%	1	15	1.00	200	1.600.15	0.800.15	0.800.15	0.300.20

Item	Specifications	Test Methods
Solder- Ability	More than 90% of termination should be covered with new solder.	Solder: Sn, Temperature: 255+5/-0, Flux: rosin, Duration: 3.50.5s
Leaching Resistance	More than 75% of termination Should be covered with new solder.	Solder: Sn, Temperature: 270+2/-0, Flux: rosin, Duration: 100.5s
Bending Strength	No mechanical damage should be noticed	When the board curve to 2mm (0.079 inch)
Body Strength	No mechanical damage should be noticed	Applied specified pull strength in axial direction
Terminal Strength	The terminal and body should be no damage	Applied specified pull strength in axial
Drop	1.No mechanical damage shall be noticed 2. Inductance shall be within 0.001H ~ 10H: 10%; 10H ~ 220H: 20%	Drop 10 times on a concrete floor from a height of 1m.
Vibration	Inductance shall be within 0.001H ~ 10H: 10%; 10H ~ 220H: 20%	Frequency: 10 to 55Hz, Amplitude: 1.52mm, Direction and time: X, Y and Z directions for 2 hours each.
Humidity resistance	Inductance shall be within 0.001H ~ 10H: 10%; 10H ~ 220H: 20%	Temp.: 602 , Humidity: 90%~95%, Test time: 1000 h. Stabilize at normal condition for 24 hours before test.
High temperature resistance	Inductance shall be within 0.001H ~ 10H: 10%; 10H ~ 220H: 20%	Applied rated current, Temp.: 1252, Test time: 1000 h. Stabilize at normal condition for 24 hours before test.
Low temperature resistance	Inductance shall be within 0.001H ~ 10H: 10%; 10H ~ 220H: 20%	Temp.: -552, Test time: 1000 h. Stabilize at normal condition for 24 hours before test.
Thermal shock	Inductance shall be within 0.001H ~ 10H: 10%; 10H ~ 220H: 20%	1) Temp.: -55, time: 303min; 2) Temp.: +125, time: 303min; 100 cycles. Stabilize at normal condition for 24 hours before test.