Ceramic Capacitors muRata GRM188R61E106KA73D 10uF 25V 0603 Package X5R Temperature Characteristics

Price Negotiable

Price: Negotiable

MOQ: Negotiable

Delivery Time: Negotiable

Product Description

Product Overview

This product specification applies to Chip Multilayer Ceramic Capacitors for General Electronic equipment. These capacitors are designed for general-purpose applications, offering reliable performance in a compact 0603 package.

Product Attributes

Brand: MURATA
Origin: Not specified
Material: Ceramic
Color: Not specified
Certifications: Not specified

Technical Specifications

Part Number	Size Code	Temperature Characteristics	Capacitance	Capacitance Tolerance	Rated Voltage (DC)	Dimensions (L x W x T) (mm)	Packaging	Packaging Code
GRM188R61E106KA73	0603	X5R (EIA)	10uF	+/-10%	25 V	0.6 x 0.3 x 0.3 (approx.)	4000 pcs./Reel	W8P4
GRM188R61E106KA73	0603	X5R (EIA)	10uF	+/-10%	25 V	0.6 x 0.3 x 0.3 (approx.)	10000 pcs./Reel	W8P4

Specifications and Test Methods

Item	Specification	Test Method
Rated Voltage	25 V	Shown in Rated value.
Insulation Resistance (I.R.)	More than 50F	Room Temperature, Rated Voltage, 1min charging time.
Capacitance	10uF	Room Temperature, 1.0+/-0.1kHz, 1.0+/-0.2Vrms. Pre-treatment: 150C for 1 hour, then 24 hours at room temperature.
Q or Dissipation Factor (D.F.)	0.1 max.	Room Temperature, 1.0+/-0.1kHz, 1.0+/-0.2Vrms.
Capacitance Change (Temperature Characteristics)	+/-15% (Max. Operating Temp. to Ref. Temp.)	Measured after 5 minutes at each specified temperature stage. Pre-treatment: 150C for 1 hour, then 24 hours at room temperature.
Adhesive Strength of Termination	No removal or defect	Solder on test substrate, 5N applied force, 10s holding time.
Vibration	Capacitance: Within specified initial value. Q or D.F.: Within specified initial value.	10Hz to 55Hz to 10Hz, 1.5mm total amplitude, 2 hours in each of 3 directions.
Substrate Bending Test	Capacitance: Within +/-10%	Flexure: 1mm, Holding Time: 5s.
Solderability	95% of terminations soldered evenly and continuously.	Solder bath method, Sn-3.0Ag-0.5Cu, 245C, 2s.
Resistance to Soldering Heat	Capacitance: Within +/-15%. Q or D.F.: Within specified initial value. I.R.: Within specified initial value.	Solder bath method, Sn-3.0Ag-0.5Cu, 270C, 10s.
Temperature Sudden Change	Capacitance: Within +/-7.5%. Q or D.F.: Within specified initial value. I.R.: Within specified initial value. Voltage Proof: No defects.	5 cycles of temperature changes. Pre-treatment: 150C for 1 hour, then 24 hours at room temperature. Post-treatment: 24 hours at room temperature.
High Temperature High Humidity (Steady)	Capacitance: Within +/-12.5%. Q or D.F.: DF:0.2 max. I.R.: More than 500M or 12.5F (whichever is smaller).	40C, 90%-95%RH, 500h. Test Voltage: Rated Voltage. Pre-treatment: 150C for 1 hour, then 24 hours at room temperature. Post-treatment: 150C for 1 hour, then 24 hours at room temperature.
Durability	Capacitance: Within +/-12.5%. Q or D.F.: DF:0.2 max. I.R.: More than 1000M or 25F (whichever is smaller).	Maximum Operating Temperature, 1000h. Test Voltage: 150% of rated voltage. Pre-treatment: 150C for 1 hour, then 24 hours at room temperature. Post-treatment: 150C for 1 hour, then 24 hours at room temperature.