Chip Ferrite Bead muRata BLM18HE601SN1D for Effective Noise Control in Electronic Applications

Price Negotiable

Price: Negotiable

MOQ: Negotiable

Delivery Time: Negotiable

Product Description

Product Overview

The BLM18H_SN Series Chip Ferrite Bead is designed for noise suppression in electronic circuits. It offers effective impedance characteristics at high frequencies, making it suitable for various applications including general use, large current, high-speed signal lines, and digital interfaces. The product is designed for solder mounting and adheres to standard testing conditions for electrical and mechanical performance.

Product Attributes

Brand: MURATA MFG.CO.,LTD.
Product ID: BLM
Packaging: D:Taping / B:Bulk
RoHS Marking: ROHS Y ()

Technical Specifications

MURATA Part Number	Impedance () at 100MHz	Impedance () at 1GHz	Rated Current (mA) at 85	Rated Current (mA) at 125	DC Resistance ( max.)	Remark
BLM18HE601SN1D	60025%	300 min.	600 *1	800 *1	0.25	For Large Current
BLM18HE601SN1B	60025%	300 min.	600 *1	800 *1	0.25	For Large Current
BLM18HE102SN1D	100025%	500 min.	1000 *1	600 *1	0.35
BLM18HE102SN1B	100025%	500 min.	1000 *1	600 *1	0.35
BLM18HE152SN1D	150025%	750 min.	1500 *1	500 *1	0.50
BLM18HE152SN1B	150025%	750 min.	1500 *1	500 *1	0.50
BLM18HG471SN1D	47025%	400 min.	600	200	0.85	For general use
BLM18HG471SN1B	47025%	400 min.	600	200	0.85	For general use
BLM18HG601SN1D	60025%	450 min.	700	200	1.0
BLM18HG601SN1B	60025%	450 min.	700	200	1.0
BLM18HG102SN1D	100025%	750 min.	1000	100	1.6
BLM18HG102SN1B	100025%	750 min.	1000	100	1.6
BLM18HD471SN1D	47025%	700 min.	1000	100	1.2	For high speed signal line
BLM18HD471SN1B	47025%	700 min.	1000	100	1.2	For high speed signal line
BLM18HD601SN1D	60025%	850 min.	1200	100	1.5
BLM18HD601SN1B	60025%	850 min.	1200	100	1.5
BLM18HD102SN1D	100025%	1100 min.	1700	50	1.8
BLM18HD102SN1B	100025%	1100 min.	1700	50	1.8
BLM18HB121SN1D	12025%	50040%	200	0.5	0.5
BLM18HB121SN1B	12025%	50040%	200	0.5	0.5
BLM18HB221SN1D	22025%	110040%	100	0.8	0.8
BLM18HB221SN1B	22025%	110040%	100	0.8	0.8
BLM18HB331SN1D	33025%	160040%	50	1.2	1.2
BLM18HB331SN1B	33025%	160040%	50	1.2	1.2
BLM18HK331SN1D	33025%	40040%	200	0.5	0.5	For Digital Interface
BLM18HK331SN1B	33025%	40040%	200	0.5	0.5	For Digital Interface
BLM18HK471SN1D	47025%	60040%	200	0.7	0.7
BLM18HK471SN1B	47025%	60040%	200	0.7	0.7
BLM18HK601SN1D	60025%	70040%	100	0.9	0.9
BLM18HK601SN1B	60025%	70040%	100	0.9	0.9
BLM18HK102SN1D	100025%	120040%	50	1.5	1.5
BLM18HK102SN1B	100025%	120040%	50	1.5	1.5

Item	Specification	Test Method
Operating Temperature	-55C to +125C
Storage Temperature	-55C to +125C
Impedance Measuring Frequency	100MHz1MHz , 1GHz1MHz
DC Resistance Measuring Equipment	Digital multi meter
Appearance and Dimensions	Meet item 4.	Visual Inspection and measured with Slide Calipers.
Bonding Strength	Table 1.	Soldered on substrate. Applying Force(F) : 6.8N, Applying Time : 5s1s, Applied direction:Parallel to substrate
Bending Strength	Table 1.	Soldered on substrate. Substrate: Glass-epoxy 100mm40mm1.0mm, Deflection : 2.0mm, Speed : 0.5mm/s, Keeping Time : 30s
Vibration		Soldered on substrate. Oscillation Frequency : 10Hz to 55Hz to 10Hz for 1 min, Total Amplitude : 1.5mm, Testing Time : 2 hours in each of 3 mutually perpendicular directions.
Resistance to Soldering Heat		Pre-Heating : 150C10C, 60s90s, Solder : Sn-3.0Ag-0.5Cu, Solder Temperature : 270C5C, Immersion Time : 10s0.5s
Drop	No failure	Free fall on concrete or steel board. Height : 75cm, Attitude : 3 directions, Number of times : 3 times for each direction.
Solderability	Electrodes at least 95% covered with new solder coating.	Flux : Ethanol solution of rosin,25(wt)%, Pre-Heating : 150C10C, 60s90s, Solder : Sn-3.0Ag-0.5Cu, Solder Temperature : 240C5C, Immersion Time : 3s1s
Temperature Cycle	Table 1.	1 cycle: -55C / 30min3min, Ordinary temp. / 10min to 15min, +125C / 30min3min, Ordinary temp. / 10min to 15min. Total of 100 cycles.
Humidity		Temperature : 40C2C, Humidity : 90%(RH) to 95%(RH), Time : 1000h(+48h,-0h)
Heat Life	Table 2.	Temperature : 125C3C, Applying Current : Rated Current (at 125C), Time : 1000h(+48h,-0h)
Cold Resistance	Table 1.	Temperature : -552C, Time : 1000h(+48h,-0h)