Large Current Chip Multilayer Ceramic Capacitor muRata NFM15PC105R0G3D 1uF DC4V 0402 Package Low ESL

Price Negotiable

Price: Negotiable

MOQ: Negotiable

Delivery Time: Negotiable

Product Description

Product Overview

The NFM15PC105R0G3 is a Large Current 3 Terminals Low ESL Chip Multilayer Ceramic Capacitor (EMIFIL) designed for general electronic equipment. It offers low ESL and is suitable for applications requiring high reliability.

Product Attributes

Brand: MURATA
Type: Chip Multilayer Ceramic Capacitors (EMIFIL)
Packaging: 0402, 1uF, DC4V

Technical Specifications

Item	Specification	Test Method
Nominal Capacitance	1 uF
Capacitance Tolerance	±20 %
DC Rated Voltage	DC 4 V
Rated Current (DC)	2A
DC Resistance	30mΩmax.	Measured with 100mA max.
Insulation Resistance	500MΩmin.
Operating Temperature Range	-55 to 85 °C
Storage Temperature Range	-55 to 85 °C
Dimensions (L x W x T)	1.0±0.05 x 0.5±0.1 x 0.3±0.05 mm	Using calipers
Capacitance Measurement Frequency	1.0±0.1kHz
Capacitance Measurement Voltage	0.5V±0.1V(rms) for [NFM15PC474/105/435]
Withstanding Voltage Test	Rated Voltage x 300% for 1 to 5 s
Solderability	Electrodes shall be at least 90% covered with new solder coating.	Ethanol solution of rosin, 25(wt)%, Pre-heat: 150±10°C, 60 to 90s, Solder: Sn-3.0Ag-0.5Cu, Solder Temperature: 240 ± 3°C, Immersion Time: 3±1 s
Resistance to soldering heat	Appearance No damaged, Cap. Change Within ±7.5%, DC Resistance 0.05Ωmax.	Ethanol solution of rosin, 25(wt)%, Pre-heat: 150±10°C, 60 to 90s, Solder: Sn-3.0Ag-0.5Cu, Solder Temperature: 270 ± 5°C, Immersion Time: 10 ± 1 s
Bending Strength	Deflection 1.0 mm	Soldered on glass-epoxy substrate (100×40×0.8mm)
Drop Test	Height 1m	Dropped on concrete or steel board, Free fall, 3 directions
Bonding Strength	Applying Force (F): 5 N	Soldered on glass-epoxy substrate, Applying Time: 10 s
Vibration Test	Total amplitude 3.0 mm or Acceleration amplitude 196m/s² whichever is smaller.	Soldered on glass-epoxy substrate, Oscillation Frequency: 10 to 2000 to 10Hz for 20 minute, 2 hours in each of 3 mutually perpendicular directions.
Temperature Cycling	Appearance No damaged, Cap. Change Within ±12.5%, I.R. Meet the initial rated value, DC Resistance 0.05Ωmax.	Soldered on glass-epoxy substrate, 10 cycles
Humidity Test	Appearance No damaged, Cap. Change Within ±12.5%, I.R. 105MΩmin. (for 473,104,224,474,105), 25MΩmin. (for 435), 5MΩmin. (for 755,915), DC Resistance 0.05Ωmax.	Soldered on glass-epoxy substrate, Temperature: 40±2°C, Humidity: 90 to 95%(RH), Time: 500+24 / -0 hours
Heat Life Test	Appearance No damaged, Cap. Change Within ±12.5%, I.R. 105MΩmin. (for 473,104,224,474,105), 25MΩmin. (for 435), 5MΩmin. (for 755,915), DC Resistance 0.05Ωmax.	Soldered on glass-epoxy substrate, Temperature: Maximum Operating Temperature ± 2 °C, Test Voltage: Rated Voltage x 150%, Time: 1000+48 / -0 hours
Packaging Unit	10000 pcs./Reel (PAPER Tape)