Multilayer Ceramic Capacitor SAMWHA CS2012X7R225K500NRE Commercial Grade Thin Layer Large Capacitance Type IEC60384

Price Negotiable

Price: Negotiable

MOQ: Negotiable

Delivery Time: Negotiable

Product Description

SAMWHA CAPACITOR CO., LTD. - MULTILAYER CERAMIC CAPACITOR

Product Description: This document details the Multilayer Ceramic Capacitor, Commercial Grade (Thin Layer Large-Capacitance Type), qualified to IEC-60384 standards. These capacitors are primarily designed for use in computer and communication equipment. Applications for industrial equipment, high reliability equipment, and LED equipment may require further consultation with sales representatives or product engineers.

Product Attributes

Brand: SAMWHA CAPACITOR CO., LTD.
Product Type: Multilayer Ceramic Capacitor
Grade: Commercial Grade
Type: Thin Layer Large-Capacitance Type
Certifications: IEC-60384 Qualified
Origin: KOREA

Technical Specifications

Part Number	Type Designation	Capacitance	Capacitance Tolerance	Dissipation Factor (Max.)	Insulation Resistance (Min.)	Chip Size (L x W x T) mm	Temperature Coefficient	Voltage (DC)	Termination	Packing
CS2012X7R225K500NRE	CS2012X7R225K500NRE	2.2	10 %	12.5 %	22.7	2.00 0.20 x 1.25 0.15 x 1.25 0.15	X7R (-55 to +125, 15%)	50V DC	Ni-Sn (Nickel-Tin Plate)	7" Reel Type

Item	Specification	Test Methods and Conditions
Operating Temperature Range	X7R: -55 to +125
Insulation Resistance	50F min	Applied the rated voltage for 2 minutes of charging. The charge/discharge current is less than 50mA.
Voltage proof	X7R: The rated voltage 250% - Applied between the terminations for 1 to 5 seconds.	The charge/discharge current is less than 50mA.
Capacitance	Within the specified tolerance	Measured at 25, 1 0.1kHz, 1 0.2Vrms (for C10)
Dissipation Factor	X7R: 12.5%max
Solderability	95% of the terminations is to be soldered evenly and continuously.	Pb-Free type Solder: 96.5Sn-3Ag-0.5Cu, Solder temperature: 2455, Immersion time: 30.1sec, Pre-Heating: at 80~120 for 10~30sec
Resistance to Soldering Heat	Capacitance change: Within 7.5%	Preheat the capacitor at 120 to 150 for 1 minute. Immerse the capacitor in a eutectic solder solution at 2605 for 100.5 seconds. Let sit at room temperature for 242 hours, then measure.
Rapid change of temperature	Capacitance Change X7R: Within 7.5%	Perform five cycles according to heat treatments. Let sit at room temperature for 242 hours, then measure.
Endurance	Capacitance Change X7R: Within 12.5%	Apply 150% of the rated voltage for 1000+48/-0 hrs at the maximum operating temperature 3. Let sit at room temperature for 242 hours, then measure.
Substrate bending test	Capacitance Change X7R: Within 10%	Substrate material: Glass EPOXY Board. Thickness: 1.6. Bending limit: 1mm, Pressurizing speed: 1mm/sec, Holding time: 51sec.
Vibration	Capacitance within the specified tolerance	Subjected to simple harmonic motion, 1.5mm amplitude, 10 to 55Hz, for 2 hours in each of 3 mutually perpendicular directions. After soldering and then let sit for 242hr at room temperature.
Accelerated damp heat, steady state	Capacitance Change X7R: Within 12.5%	Apply the rated voltage at 402 and 90 to 95%RH for 500+24/-0 hrs. Let sit at room temperature for 242 hours, then measure.
Temperature characteristic of capacitance	X7R: Within 15%	Measured after 5 min. at each specified temperature stage. Compared with the 25 value over the temperature ranges (-55 to +125).