BOPP Film Roll

Name Specification Application CLEAR FILMS Non-heat sealable 12-75mic Tape, floral, labels, stationery, overlaminated, Insulation, metallizing, etc. Heat-sealable(1, 2 sides) 15-50mic Over wrap, form/fill/seal, bakery, printing lamination, metallizing, etc. MATTE FILMS Non-heat sealable 12-50mic Tape, floral, over lam, labels, etc. Heat sealable(1, 2 sides) 15-50mic Over lam, lamination, over wrap,

Bopp Film SPECIFICATION PARAMETER SPECIFICATION 24 GLOSS 25 GLOSS 27 GLOSS 30 GLOSS 26 MATT 27 MATT 28 MATT 30 MATT THICKNESS(UM) BASE 12 12 15 18 15 15 17 18 EVA 12 13 12 12 11 12 11 12 TOTAL 24 25 27 30 26 27 28 30 WEIGHT kg 45.04 43.22 40.1 36.15 42.37 41.35 39.25 37.37 kg 0.222 0.0231 0.025 0.02766 0.0236 0.02418 0.02548 0.02676 Width 360 390 440 540 590 780 880 1080 1320 1400 1600 1800 Upon customer's

No. Item Unit Result 1 Width Bias mm 0 2 Thickness Bias % -0.93 3 Average Thickness Bias % 0.64 4 Tensile Strength MD Mpa 182.6 TD 295.3 5 Elongation MD % 158.5 TD 59.2 6 Modulus (Reference Value) MD Mpa 2033.82 7 Heat shrinkage MD % 3.5 TD 3.9 8 Haze % 1.72 9 Gloss % 96.2 10 Decaying rate of static Treated side 　 22.32 No-treated side 　 20.58 11 COF(q/m) Outside/Metal 　 0.218/0.146 Inside/ Metal 　 0

Test Item Unit Standard Value Test Standard Thickness Deviation % 0.3 ASTM E 252 Corona Treatment mN/m ≥38 ASTM D 2578 Tensile Strength MD MPa ≥140 ASTM D 882 TD ≥200 Elongation MD % ≤180 ASTM D 882 TD ≤65 E-Modulus MD MPa ≥1800 ASTM D 882 COF MD -- ≤0.8 ASTM D 1849 Shrinkage MD % ≤4 BMS TT 01 TD ≤2 Haze % ≤1.5 ASTM D 1003 Gloss % ≥85 ASTM D 2457 Width mm 0-+2 GB6673-86 The abbreviation of BOPP is "Biaxially

Cigarette packaging film has the characteristics of high smoothness, heat sealing effect, good opening, good shrinkage performance. It is mainly used for the packaging of soft box, hard box and strip cigarette. The cigarette packaging film of our company is made of BOPP, which has the advantages of light weight, non-toxic, odorless, moisture-proof, high mechanical strength, good dimensional stability, good

Cigarette BOPP film has advantages of high transparency, good gloss, good barrier properties, high impact strength and low temperature resistance. Its overall performance is better than moisture-proof cellophane, polyethylene (PE) film, PET film. BOPP film also has excellent printing results. It can be laminated with other special materials to further improve its performance. BOPP film is extremely competitiv

NO. Product Property Detail & Description 1 Material BOPP 2 Thickness 18 um – 25 um 3 Width 117mm, 119mm, 120mm, 170mm, 340mm, 345mm, 350mm, 360mm (customized as per request) 4 Length 2000 – 4000m 5 ID of Inner Core 76mm 6 Shrinkage 1%-3%(Low Shrinkage); 4%-6%(Middle Shrinkage); 7%-10%(High Shrinkage) 7 Density 0.905 g/cm³, 0.92 g/cm³ 8 Thickness 22.0 μ m, 21.0 μ m 9 Tensile Strength(MD) 150 N/mm, 175 N

Anti-Static Property BOPP Transparent Film For Cigarette Cases Pack 120mm Property Unit Test Method Block Copolymer Random Copolymer Homopolymer Grade 2309KX 3200 MCX 3520 LX 1125N 1127MX 1325L Additives None None Antiblock agents Slip, antiblock agents Slip, antiblock agents Slip, antiblock agents Melt flow rate g/10 min ISO 1133 4 8 5 11 8 5 Gloss 20° % DIN 67530 5 130 130 110 95 115 Haze % ASTM 1003 28 0.5 0.3 2.3 3.0 1.7 Tensile strength at break Machine Direction MPa DIN

Test Item Unit Standard Value Test Standard Thickness Deviation % 0.3 ASTM E 252 Corona Treatment mN/m ≥38 ASTM D 2578 Tensile Strength MD MPa ≥140 ASTM D 882 TD ≥200 Elongation MD % ≤180 ASTM D 882 TD ≤65 E-Modulus MD MPa ≥1800 ASTM D 882 COF MD -- ≤0.8 ASTM D 1849 Shrinkage MD % ≤4 BMS TT 01 TD ≤2 Haze % ≤1.5 ASTM D 1003 Gloss % ≥85 ASTM D 2457 Width mm 0-+2 GB6673-86 Wide Range of Application

NO. Product Property Detail & Description 1 Material BOPP 2 Thickness 18 um – 25 um 3 Width 117mm, 119mm, 120mm, 170mm, 340mm, 345mm, 350mm, 360mm (customized as per request) 4 Length 2000 – 4000m 5 ID of Inner Core 76mm 6 Shrinkage 1%-3%(Low Shrinkage); 4%-6%(Middle Shrinkage); 7%-10%(High Shrinkage) 7 Density 0.905 g/cm³, 0.92 g/cm³ 8 Thickness 22.0 μ m, 21.0 μ m 9 Tensile Strength(MD) 150 N/mm, 175 N/mm, 160N/mm

Test Item Unit Standard Value Test Standard Thickness Deviation % 0.3 ASTM E 252 Corona Treatment mN/m ≥38 ASTM D 2578 Tensile Strength MD MPa ≥140 ASTM D 882 TD ≥200 Elongation MD % ≤180 ASTM D 882 TD ≤65 E-Modulus MD MPa ≥1800 ASTM D 882 COF MD -- ≤0.8 ASTM D 1849 Shrinkage MD % ≤4 BMS TT 01 TD ≤2 Haze % ≤1.5 ASTM D 1003 Gloss % ≥85 ASTM D 2457 Width mm 0-+2 GB6673-86 BOPP heat sealing film is divided

TDS Property ASTM Test Method Cast, Uniaxial Orientation Area factor in 2/lb./1 mil film – 30,400–31,300 Specific gravity (g/cm3) D1505 0.885–0.905 Tensile strength (psi) D882 4500–7000 Elongation (%) D882 550–1000 Tear strength (g/mil propagation) D1922 25 MD 600 TD Fold Endurance D2176 Very high 24 h % water absorption D570 0.005 Water vapor transmission rate (g/mil/100 in.2/24 h at 100°F) E96 0.7

Property ASTM Test Method Cast, Uniaxial Orientation Biaxial Orientation Area factor in 2/lb./1 mil film – 30,400–31,300 30,600 Specific gravity (g/cm3) D1505 0.885–0.905 0.902–0.907 Tensile strength (psi) D882 4500–7000 7500–40,000 Elongation (%) D882 550–1000 352475 Tear strength (g/mil propagation) D1922 25 MD 600 TD 3–10 Fold endurance D2176 Very high Excellent 24 h % water absorption D570 0.005 0

Clean BOPP Film Roll Surface Cigarette Boxes Packing No Bubble No Wrinkle Specification Of BOPP Thermal Lamination Film Item Thickness(mic) Ration/yield Resistance Type Total Tolerance G/M2 G/25MM Glossy 17 17 (+/-) 1.5mic 15.68 560 20 20 18.43 560 25 25 22.65 580 27 27 24.95 620 30 30 27.67 630 Matt 17 17 14.81 580 23 23 19.89 580 27 27 24.19 620 30 30 27.24 680 Biaxially oriented polypropylene (BOPP) film is film stretched in both machine and transverse directions,

Raw material: BOPP Thickness (um) : 30~120 Width (cm) : 5~150 Color: transparent, Adhesive force (g/25mm) : 20~400 Drawing rate (%) : 300 Tensile strength (N/25mm) : 15 Biaxially oriented polypropylene (BOPP) film is film stretched in both machine and transverse directions, producing molecular chain orientation in two directions. BOPP film is produced by a tubular process, in which a tubular bubble is

DATA: TEMS TEST METHOD UNIT TYPICAL VALUE Tensile strength MD GB/T 1040.3- 06 Mpa ≥130 TD ≥250 Elongation at break MD GB/T 1040.3- 06 % ≤180 TD ≤65 Thermal shrinkage MD GB/T 12027 04 % ≤4.0 TD ≤2.5 Friction coefficient Treated side GB/T 10006.88 /

Bopp thermal lamination film (Gloss Matt) SPECIFICATION PARAMETER SPECIFICATION 24 GLOSS 25 GLOSS 27 GLOSS 30 GLOSS 26 MATT 27 MATT 28 MATT 30 MATT THICKNESS(UM) BASE 12 12 15 18 15 15 17 18 EVA 12 13 12 12 11 12 11 12 TOTAL 24 25 27 30 26 27 28 30 WEIGHT kg 45.04 43.22 40.1 36.15 42.37 41.35 39.25 37.37 kg 0.222 0.0231 0.025 0.02766 0.0236 0.02418 0.02548 0.02676 Width 360 390 440 540

NO INDEX UNIT STANDARD VALUE Micro Shrinkage Middle Shrinkage High Shrinkage General 1 TENSILE STRENORH MD MPa ≥140 ≥140 ≥140 ≥140 TD ≥220 ≥220 ≥220 ≥220 2 Elongation MD % ≤180 ≤180 ≤180 ≤180 TD ≤70 ≤70 ≤70 ≤70 3 Shrinkage MD % 4.0-5.5 5.5-7.5 >7.5 ≤4.0 TD 4.0-6.0 6.0-8.5 >8.5 ≤4.0 4 E-Modulus MD MPa ≥2000 ≥2100 ≥2400 ≥2000 5 HAZE % ≤2.0 ≤2.0 ≤1.5 ≤2.0 6 COF ≤0.28 ≤0.28 ≤0.28 ≤0.28 7 Sealing

Material BOPP Feature Moisture Proof PHR (handfeel) 20 - 60 MOQ 1000 Kilograms Transparency Translucent or Opaque Thickness 0.08 – 0.3mm Payment terms L/C, T/T, D/P Width 120mm – 360mm, or Wider Type Calendering film Length To order Certification lower toxicity, EN-71, REACH, ROHS and etc. Delivery Time 7 days after received deposit or L/C/T.T Usage Using for cigarette boxes with high clear finished Cigarette

Tech Data for Reference : BOPP Film TYPICAL PROPERTIES UNIT TEST METHODS TYPICAL VALUE THICKNESS micron Micrometer 25 　 　 　 YIELD m2/kg (min.) - 59 49 42 35 28 DENSITY g/cm3 ASTM D-1505 0.65-0.70 0.65-0.70 0.65-0.70 0.68-0.72 0.68-0.72 TENSILE STRENGTH kg/mm2 MD ASTM 6 6 6 6 6 (min.) TD D-882 12 12 12 12 12 ELONGATION AT BREAK % MD ASTM 140 140 140 140 140 (max.) TD D-882 50 50 50 50 50 THERMAL SHRINKAGE % MD ASTM