BOPP Film Roll

NO. Product Property Detail & Description 1 Material BOPP 2 Thickness 18 um – 25 um 3 Width 117mm, 119mm, 120mm, 170mm, 340mm, 345mm, 350mm, 360mm (customized as per request) 4 Length 2000 – 4000m 5 ID of Inner Core 76mm 6 Shrinkage 1%-3%(Low Shrinkage); 4%-6%(Middle Shrinkage); 7%-10%(High Shrinkage) 7 Density 0.905 g/cm³, 0.92 g/cm³ 8 Thickness 22.0 μ m, 21.0 μ m 9 Tensile Strength(MD) 150 N/mm, 175 N

Superslim 122mm Size Cigarette BOPP Film Static-Free Bopp Film SPECIFICATION PARAMETER SPECIFICATION 24 GLOSS 25 GLOSS 27 GLOSS 30 GLOSS 26 MATT 27 MATT 28 MATT 30 MATT THICKNESS(UM) BASE 12 12 15 18 15 15 17 18 EVA 12 13 12 12 11 12 11 12 TOTAL 24 25 27 30 26 27 28 30 WEIGHT kg 45.04 43.22 40.1 36.15 42.37 41.35 39.25 37.37 kg 0.222 0.0231 0.025 0.02766 0.0236 0.02418 0.02548 0.02676 Width 360 390 440 540 590 780 880 1080 1320 1400 1600 1800 Upon customer's requirement

Test Item Unit Standard Value Test Standard Thickness Deviation % 0.3 ASTM E 252 Corona Treatment mN/m ≥38 ASTM D 2578 Tensile Strength MD MPa ≥140 ASTM D 882 TD ≥200 Elongation MD % ≤180 ASTM D 882 TD ≤65 E-Modulus MD MPa ≥1800 ASTM D 882 COF MD -- ≤0.8 ASTM D 1849 Shrinkage MD % ≤4 BMS TT 01 TD ≤2 Haze % ≤1.5 ASTM D 1003 Gloss % ≥85 ASTM D 2457 Width mm 0-+2 GB6673-86 BOPP thermal laminating

Property Unit Test Method Block Copolymer Random Copolymer Homopolymer Grade 2309KX 3200 MCX 3520 LX 1125N 1127MX 1325L Additives None None Antiblock agents Slip, antiblock agents Slip, antiblock agents Slip, antiblock agents Melt flow rate g/10 min ISO 1133 4 8 5 11 8 5 Gloss 20° % DIN 67530 5 130 130 110 95 115 Haze % ASTM 1003 28 0.5 0.3 2.3 3.0 1.7 Tensile strength at break Machine direction MPa

Introduction: BOPP Thermal Laminating Film is mainly made of BOPP + EVA. We use extrusion-coating process to combine these two layers. In the final film one side has properties of BOPP film and the other side becomes heat sensitive surface used for dry lamination. This product has two classifications: glossy/shine/transparent and matte/opaque, both of which sees thickness from 14micron to 32micron.

Introduction: BOPP Thermal Laminating Film is mainly made of BOPP + EVA. We use extrusion-coating process to combine these two layers. In the final film one side has properties of BOPP film and the other side becomes heat sensitive surface used for dry lamination. This product has two classifications: glossy/shine/transparent and matte/opaque, both of which sees thickness from 14micron to 32micron. Its

Introduction: 1. Enhance the finished product's value through high transparency and super gloss finish. Prevent lamination from being pressed, bubbled and desquamated. Protect from harmful substances and water-proof, making long life storage for printings. 2. Available in various paper and inks, and suitable for lamination even with powder paper. After be treated with corona on the surface, it is good

Introduction: Biaxially oriented polypropylene (BOPP) film is film stretched in both machine and transverse directions, producing molecular chain orientation in two directions. BOPP film is produced by a tubular process, in which a tubular bubble is inflated, or a tenter frame process, in which a thick extruded sheet is heated to its softening point (not to the melting point) and is mechanically

Introduction: Biaxially oriented polypropylene (BOPP) film is film stretched in both machine and transverse directions, producing molecular chain orientation in two directions. BOPP film is produced by a tubular process, in which a tubular bubble is inflated, or a tenter frame process, in which a thick extruded sheet is heated to its softening point (not to the melting point) and is mechanically

Introduction: Biaxially oriented polypropylene (BOPP) film is film stretched in both machine and transverse directions, producing molecular chain orientation in two directions. BOPP film is produced by a tubular process, in which a tubular bubble is inflated, or a tenter frame process, in which a thick extruded sheet is heated to its softening point (not to the melting point) and is mechanically stretched

Introduction: BOPP Thermal Laminating Film is mainly made of BOPP + EVA. We use extrusion-coating process to combine these two layers. In the final film one side has properties of BOPP film and the other side becomes heat sensitive surface used for dry lamination. This product has two classifications: glossy/shine/transparent and matte/opaque, both of which sees thickness from 14micron to 32micron. Its

Introduction: Biaxially oriented polypropylene (BOPP) film is film stretched in both machine and transverse directions, producing molecular chain orientation in two directions. BOPP film is produced by a tubular process, in which a tubular bubble is inflated, or a tenter frame process, in which a thick extruded sheet is heated to its softening point (not to the melting point) and is mechanically stretched

Introduction: Its comprehensive performance is superior to moisture-proof cellophane, polyethylene (PE) film, and PET film. BOPP film also has excellent printing effects. The representative physical property data are: turbidity 85%; tensile strength (longitudinal / transverse)> 120 / 200MPa; elongation at break (longitudinal / transverse)

Introduction: Biaxially oriented polypropylene (BOPP) film is film stretched in both machine and transverse directions, producing molecular chain orientation in two directions. BOPP film is produced by a tubular process, in which a tubular bubble is inflated, or a tenter frame process, in which a thick extruded sheet is heated to its softening point (not to the melting point) and is mechanically

Introduction: High transparency, good gloss, good printability It is non-toxic, odorless and tasteless, and can be directly used in contact with food and medicine. Due to the molecular orientation, the crystallinity is improved, the tensile strength, impact strength, rigidity, toughness, moisture resistance and transparency are all improved, and the cold resistance of the film is also improved. Good

Introduction: High transparency, good gloss, good printability It is non-toxic, odorless and tasteless, and can be directly used in contact with food and medicine. Due to the molecular orientation, the crystallinity is improved, the tensile strength, impact strength, rigidity, toughness, moisture resistance and transparency are all improved, and the cold resistance of the film is also improved. Good gas

Introduction: In the final film one side has properties of BOPP film and the other side becomes heat sensitive surface used for dry lamination. This product has two classifications: glossy/shine/transparent and matte/opaque, both of which sees thickness from 14micron to 32micron. Its width could be from 180mm to 1880mm and length from 150m (1 inch core, 25mm) to 4000m (3 inch core, 76mm). High

Introduction: BOPP Oriented films can be used as heat-shrinkable films in shrink-wrap applications or can be heat set to provide dimensional stability. Heat sealing is difficult in BOPP films, but can be made easier by either coating the film after processing with a heat-sealable material (such as polyvinylidene chloride) or by coextrusion with one or more copolymers before processing to produce layers

Introduction: 25mic=12mic (bopp film) +13mic (EVA glue) 27mic=15mic (bopp film) +12mic (EVA glue) 30mic=15mic (bopp film) +15mic (EVA glue) (1) Books and magazines, pictures, promotional materials; non-drying adhesive, paper bag, clothes bag, liquor, food, cosmetic, medicine wrapping box (2) Blueprint document, outdoor advertisement, spray paintings, post, digital print (3) Wedding photograph, photo

Introduction: High transparency, good gloss, good printability It is non-toxic, odorless and tasteless, and can be directly used in contact with food and medicine. Due to the molecular orientation, the crystallinity is improved, the tensile strength, impact strength, rigidity, toughness, moisture resistance and transparency are all improved, and the cold resistance of the film is also improved. Good