Valox Plastic

S-Plastic Valox M7002 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 33 MPa S-Plastic - Japan Method Tensile Strain, break 9 - 9 % S-Plastic - Japan Method IMPACT Value Unit Standard Izod Impact, notched, 23°C 37 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 89 °C ASTM D 648 Source GMD, last updated:06/12/2000 Processing THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR

S-Plastic Valox 7523 resin isa 45% glass/mineral filled, flame retarded PBT injection moulding resin with excellent electrical properties. ​Property MECHANICAL Value Unit Standard Tensile Stress, break, 5 mm/min 80 MPa ISO 527 Tensile Strain, break, 5 mm/min 1 % ISO 527 Tensile Modulus, 1 mm/min 11000 MPa ISO 527 Flexural Stress, break, 2 mm/min 130 MPa ISO 178 Flexural Modulus, 2 mm/min 9500 MPa ISO 178 Hardness, H358/30 144 MPa ISO 2039-1 IMPACT Value Unit Standard Izod Impact,

S-Plastic Valox 750resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 88 MPa S-Plastic - Japan Method Tensile Strain, break 3 - 3 % S-Plastic - Japan Method Flexural Stress 137 MPa ASTM D 790 Flexural Modulus 8240 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 59 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 194 °C ASTM D 648 HDT, 1.82 MPa, 3.2mm, unannealed 204 °C ASTM D 648 CTE, -30°C to 30°C 3.E-05 - 3.E-05 1/°C

S-Plastic Valox K4663 resin is a flame retardant, 30% glass reinforced injection moulding PBT resin. Applications: edge trimmers, food mixer motor stator and commutor, motor cooling fans, connectors, bobbins, switches, electrical housings/bases. This grade is a 420SE0 with reduced flame retardant performance. ​Property MECHANICAL Value Unit Standard Tensile Stress, break, 5 mm/min 138 MPa ISO 527 Tensile Strain, break, 5 mm/min 2.4 % ISO 527 Tensile Modulus, 1 mm/min 9500 MPa ISO

S-Plastic Valox 745resin is30% mineral reinforced polyester improved toughness and low warpage. Typical applications are telephone ringer frames and card racks. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 48 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 46 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 89 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 3440 MPa ASTM D 790 Hardness, Rockwell R 112 - ASTM D 785 IMPACT

S-Plastic Valox K4630 resin is 17% glass reinforced, flame retardant PBT+PC. FR ratings approved with 50% regrind approved by UL. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 99 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 102 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 3.1 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 3.3 % ASTM D 638 Tensile Modulus, 5 mm/min 4080 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span

S-Plastic Valox 736resin is 45% glass/mineral, PBTP. Nonflame retardant. Ex properties, low warpage. Motorized heating appliances, etc. In Europe: limited use, PMapproval. ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 110 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 186 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 8960 MPa ASTM D 790 Hardness, Rockwell R 116 - ASTM D 785 IMPACT Value Unit Standard Izod Impact, unnotched,

S-Plastic Valox V8560 resin isVALOX V8560 is a 30% glass reinforced, flame retardant PBT+PET blend developed to meet glow wire 750ºC/5 sec test ​Property MECHANICAL Value Unit Tensile Stress, yield, 5 mm/min 130 MPa Tensile Stress, break, 5 mm/min 130 MPa Tensile Strain, yield, 5 mm/min 2 % Tensile Strain, break, 5 mm/min 2 % Tensile Modulus, 1 mm/min 10000 MPa Flexural Stress, break, 2 mm/min 195 MPa Flexural Modulus, 2 mm/min 8000 MPa IMPACT Value Unit Izod Impact, unnotched 80

S-Plastic Valox V8531U resin is VALOX V8531U is 16% glass reinforced PBT+PET blend with improved surface appearance, UV stabilised ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 5 mm/min 85 MPa ISO 527 Tensile Stress, break, 5 mm/min 85 MPa ISO 527 Tensile Strain, yield, 5 mm/min 3 % ISO 527 Tensile Strain, break, 5 mm/min 3 % ISO 527 Tensile Modulus, 1 mm/min 6000 MPa ISO 527 Flexural Stress, break, 2 mm/min 155 MPa ISO 178 Flexural Modulus, 2 mm/min 5000 MPa

S-Plastic Valox V8530U resin is ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 10 mm/min 70 MPa S-Plastic - Japan Method Tensile Strain, brk, Type I, 10 mm/min 4.7 % S-Plastic - Japan Method Flexural Stress, brk, 2.6 mm/min, 100 mm span 5430 MPa ASTM D 790 Flexural Modulus, 2.6 mm/min, 100 mm span 90 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 27 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 1.82 MPa, 3.2mm, unannealed 184 °C ASTM D 648

S-Plastic Valox V82880SF resin is High Modulus, PBT+PET, 40% Glass Reinforced, Mold Release, Super High Flow ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 90 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 90 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 1 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 90 % ASTM D 638 Tensile Modulus, 5 mm/min 120000 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 190 MPa ASTM D 790

S-Plastic Valox 735resin is 40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/naturalonly. ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 75 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 124 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 8270 MPa ASTM D 790 Hardness, Rockwell R 109 - ASTM D 785 IMPACT Value Unit Standard Izod Impact, unnotched, 23

S-Plastic Valox K4560 resin is 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 106 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 106 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 4 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 4 % ASTM D 638 Tensile Modulus, 5 mm/min 4480 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 173 MPa ASTM D 790

S-Plastic Valox K4530 resin is 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 103 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 103 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 4 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 4 % ASTM D 638 Tensile Modulus, 5 mm/min 3550 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 150 MPa ASTM D 790

S-Plastic Valox V8280 resin is 40% GR PBT+PET. High stiffness. Excellent surface aesthetics. Applications include office furniture. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 145 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 145 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 2.2 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 2.2 % ASTM D 638 Tensile Modulus, 5 mm/min 12750 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm

S-Plastic Valox 732Eresin is 30% glass/mineral reinforced, excellent thermal performance, low shrinkage and warp. Easy flow. ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 82 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 2 % ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 124 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 6890 MPa ASTM D 790 Hardness, Rockwell R 109 - ASTM D 785 IMPACT Value Unit Standard Izod Impact,

S-Plastic Valox V5060RE resin is 34% glass reinforced PBT+PC blend with 25% recycle. Low warp automotive grade with excellent stiffness/ductility balance. ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 5 mm/min 121 MPa ISO 527 Tensile Stress, break, 5 mm/min 122 MPa ISO 527 Tensile Strain, yield, 5 mm/min 2 % ISO 527 Tensile Strain, break, 5 mm/min 2 % ISO 527 Tensile Modulus, 1 mm/min 10070 MPa ISO 527 Flexural Stress, yield, 2 mm/min 180 MPa ISO 178 Flexural

S-Plastic Valox V8090 resin is 50% Glass Fiber Reinforced PBT-PET resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 5 mm/min 175 MPa ISO 527 Tensile Stress, break, 5 mm/min 175 MPa ISO 527 Tensile Strain, yield, 5 mm/min 1.5 % ISO 527 Tensile Strain, break, 5 mm/min 1.5 % ISO 527 Tensile Modulus, 1 mm/min 17500 MPa ISO 527 Flexural Stress, yield, 2 mm/min 255 MPa ISO 178 Flexural Modulus, 2 mm/min 16000 MPa ISO 178 IMPACT Value Unit Standard Izod Impact,

S-Plastic Valox 730resin is35% glass/mineral reinforced. Low shrink. Better dimensional stability vs VALOX 420. Motorized heating appliances, etc. ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 65 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 110 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 6200 MPa ASTM D 790 Hardness, Rockwell R 82 - ASTM D 785 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C 373 J/m ASTM D 4812

S-Plastic Valox V8060RE resin is 30% glass reinforced PBT+PET blend with 25% post-consumer recycle. Hydrolitically stable. Auto specs for GM, Ford, Chrysler. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 106 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 106 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 3.8 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 3.8 % ASTM D 638 Tensile Modulus, 5 mm/min 7230 MPa ASTM D 638 Flexural Stress