S-Plastic Valox K4530 15% Glass Reinforced PBT Hydrolytically Stable High Flow Automotive Connectors

Name: S-Plastic Valox K4530 15% Glass Reinforced PBT Hydrolytically Stable High Flow Automotive Connectors
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Valox

Product Description

S-Plastics Valox K4530 resin is 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	103	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	103	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	4	% ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	4	% ASTM D 638
Tensile Modulus, 5 mm/min	3550	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	150	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	4640	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	400	J/m	ASTM D 4812
Izod Impact, notched, 23°C	58	J/m	ASTM D 256
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	218	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	193	°C	ASTM D 648
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.41	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.7 - 0.9	% S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm	1 - 1.2	% S-Plastics Method
AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	82	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2.5	% ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span	4520	MPa	ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span	9.7	% ASTM D 790
Instrumented Impact, Total Energy, 23°C	6	J	ASTM D 3763
PROPERTIES AFTER 1008 HOURS AT 125?C	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	98	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	4	% ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span	4820	MPa	ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span	7	% ASTM D 790
Instrumented Impact, Total Energy, 23°C	5	J	ASTM D 3763
AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	89	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2.3	% ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span	5100	MPa	ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span	6	% ASTM D 790
Instrumented Impact, Total Energy, 23°C	4	J	ASTM D 3763
PROPERTIES AFTER 1008 HOURS AT 155?C	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	4812	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	97.2	% ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span	0	MPa	ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span	3.8	%	ASTM D 790
Source GMD, last updated:03/25/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	60 - 75	°C
Drying Time	4 - 6	hrs
Drying Time (Cumulative)	8	hrs
Maximum Moisture Content	0.05	%
Melt Temperature	250 - 265	°C
Nozzle Temperature	245 - 260	°C
Front - Zone 3 Temperature	250 - 265	°C
Middle - Zone 2 Temperature	245 - 260	°C
Rear - Zone 1 Temperature	240 - 255	°C
Mold Temperature	65 - 90	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 80	rpm
Shot to Cylinder Size	40 - 80	%
Vent Depth	0.025 - 0.038	mm
Source GMD, last updated:03/25/2004