Valox Plastic

S-Plastic Valox 357TF resin is Unreinforced, impact modified, UL94 V-0 rated, no PTFE. Applications like film or thin gauge sheet. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 48 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 48 MPa ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 5 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 110 % ASTM D 638 Tensile Modulus, 5 mm/min 2200 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm

S-Plastic Valox EXVX1259 resin is Non chlorinated, non brominated Flame retardant 25% Glass Filled PBT ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 5 mm/min 116 MPa ISO 527 Tensile Stress, break, 5 mm/min 116 MPa ISO 527 Tensile Strain, yield, 5 mm/min 2 % ISO 527 Tensile Strain, break, 5 mm/min 2 % ISO 527 Tensile Modulus, 1 mm/min 10000 MPa ISO 527 Flexural Stress, yield, 2 mm/min 170 MPa ISO 178 Flexural Modulus, 2 mm/min 8750 MPa ISO 178 IMPACT Value Unit

S-Plastic Valox 357Mresin is Unreinforced PBTP. Easy flow. Easy release. Rated UL94 V-0. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 48 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 48 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 110 % ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 82 MPa ASTM D 790 Flexural Stress, brk, 1.3 mm/min, 50 mm span 82 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 2060 MPa ASTM D

S-Plastic Valox PDR7912 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 103 MPa S-Plastic - Japan Method Tensile Strain, break 9 - 9 % S-Plastic - Japan Method Flexural Stress 155 MPa ASTM D 790 Flexural Modulus 11170 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 66 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 208 °C ASTM D 648 CTE, -30°C to 30°C 3.E-05 - 3.E-05 1/°C TMA PHYSICAL Value Unit Standard Specific

S-Plastic Valox PDR7908 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 54 MPa S-Plastic - Japan Method Tensile Strain, break 8 - 8 % S-Plastic - Japan Method Flexural Stress 96 MPa ASTM D 790 Flexural Modulus 4250 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 42 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 1.82 MPa, 3.2mm, unannealed 192 °C ASTM D 648 CTE, -30°C to 30°C 7.E-05 - 7.E-05 1/°C TMA PHYSICAL Value Unit Standard Specific Gravity

S-Plastic Valox PDR7904 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 142 MPa S-Plastic - Japan Method Tensile Strain, break 4 - 4 % S-Plastic - Japan Method Flexural Stress 192 MPa ASTM D 790 Flexural Modulus 9770 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 102 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 192 °C ASTM D 648 HDT, 1.82 MPa, 3.2mm, unannealed 210 °C ASTM D 648 CTE, -30°C to 30°C 3.E-05 - 3.E-05

S-Plastic Valox 350U resin is Impact modified, UV stabilised, flame retardant polyester with an internal glowwire rating of 850C on 1.6mm flat plaques. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 56 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 50 MPa ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 5 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 100 % ASTM D 638 Tensile Modulus, 50 mm/min 2250 MPa ASTM D 638 Flexural Stress, yld

S-Plastic Valox EXVX1258 resin is an environmental responsible flame retarded, 30% glass fiber reinforced PBT injection moulding resin. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 106 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 106 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 1.7 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 1.7 % ASTM D 638 Tensile Modulus, 5 mm/min 11000 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50

S-Plastic Valox 340resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 40 MPa S-Plastic - Japan Method Tensile Strain, break 351 - 351 % S-Plastic - Japan Method IMPACT Value Unit Standard Izod Impact, notched, 23°C 868 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 63 °C ASTM D 648 CTE, -30°C to 30°C 1.3E-04 - 1.3E-04 1/°C TMA Source GMD, last updated:06/12/2000 　 For more information please download the datasheet S-Plastic Valox 340.pd

S-Plastic Valox 337resin is Low temperature impact PBT. Automotive applications: underhood power distribution boxes and covers. ​PropertyMECHANICALValueUnitStandardTensile Stress, yld, Type I, 50 mm/min39MPaASTM D 638Tensile Strain, yld, Type I, 50 mm/min3.9%ASTM D 638Flexural Stress, yld, 1.3 mm/min, 50 mm span56MPaASTM D 790Flexural Modulus, 1.3 mm/min, 50 mm span1790MPaASTM D 790IMPACTValueUnitStandardIzod Impact, unnotched, 23°C3204J/mASTM D 4812Izod Impact, unnotched, -30

S-Plastic Valox 334resin iscompliant with food contact regulations acc. to 90/128/EEC. VALOX 334 is a PBT injection moulding resin with improvedflow properties. This product is available in natural color only (1001). ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 50 mm/min 50 MPa ISO 527 Tensile Strain, break, 50 mm/min 30 % ISO 527 Tensile Modulus, 1 mm/min 2400 MPa ISO 527 Flexural Stress, yield, 2 mm/min 75 MPa ISO 178 Flexural Modulus, 2 mm/min 2300 MPa ISO

S-Plastic Valox 327resin is Unreinforced, impact modified polyester, high ductility and good processability. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 48 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 200 % ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 82 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 2200 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 80 J/m ASTM D 256 THERMAL Value Unit

S-Plastic Valox 325MRresin is an unreinforced general purpose injection moulding PBT resin with medium flow characteristics and internal mouldrelease. Applications : key buttons for business machines. This grade is a 325 with release. ​Property MECHANICAL Value Unit Standard Taber Abrasion, CS-17, 1 kg 9 mg/1000cy S-Plastic Method Tensile Stress, yield, 50 mm/min 55 MPa ISO 527 Tensile Stress, break, 50 mm/min 50 MPa ISO 527 Tensile Strain, yield, 50 mm/min 6 % ISO 527 Tensile Strain

S-Plastic Valox 325ML resin is Unreinforced PBTP general purpose grade. High flow characteristics for restrictive gate tooling. YAG laser markable ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 55 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 16 % ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 93 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 2270 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C 1548

S-Plastic Valox 325MFresin is PBT. Higher flow version of 325 for restrictive gate tooling. High resolution filtering. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 48 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 180 % ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 81 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 2340 MPa ASTM D 790 Hardness, Rockwell R 119 - ASTM D 785 IMPACT Value Unit Standard Izod Impact, unnotched

S-Plastic Valox 325Mresin is a high flow VALOX 325 for restrictive gate tooling (key buttons) ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 48 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 180 % ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 81 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 2340 MPa ASTM D 790 Hardness, Rockwell R 119 - ASTM D 785 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C 1602 J/m ASTM D

S-Plastic Valox 325F resin is compliant with food contact regulations acc. to a general purpose, unreinforced PBT injection moulding resin which contains internal mold release. Available in natural colour only (1001). This grade is similar to 325. ​Property MECHANICAL Value Unit Standard Taber Abrasion, CS-17, 1 kg 9 mg/1000cy S-Plastic Method Tensile Stress, yield, 50 mm/min 55 MPa ISO 527 Tensile Strain, yield, 50 mm/min 3 % ISO 527 Tensile Strain, break, 50 mm/min 60 % ISO 527

S-Plastic Valox 325E resin is General purpose, unreinforced, improved flow characteristics for restrictive tooling. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 51 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 51 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 200 % ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 82 MPa ASTM D 790 Flexural Stress, brk, 1.3 mm/min, 50 mm span 82 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min,

S-Plastic Valox 325C resin is an unreinforced, high flow PBT injection moulding resin with excellent printing properties. Applications: key caps. ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 50 mm/min 55 MPa ISO 527 Tensile Strain, yield, 50 mm/min 6 % ISO 527 Tensile Strain, break, 50 mm/min 25 % ISO 527 Tensile Modulus, 1 mm/min 2500 MPa ISO 527 Flexural Stress, yield, 2 mm/min 85 MPa ISO 178 Flexural Modulus, 2 mm/min 2400 MPa ISO 178 Hardness, H358/30 85

S-Plastic Valox 325resin is General purpose, unreinforced, improved processing. Applications like sprinklers and nozzles, pumps, door handle, tank covers, pens,pencils etc. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 51 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 200 % ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 82 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 2340 MPa ASTM D 790 Hardness, Rockwell R 117 - ASTM D