Product Description

S-Plastics Valox EXVX1258 resin is an environmental responsible flame retarded, 30% glass fiber reinforced PBT injection moulding resin.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	106	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	106	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	1.7	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.7	%	ASTM D 638
Tensile Modulus, 5 mm/min	11000	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	177	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	8950	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	97	MPa	ISO 527
Tensile Stress, break, 5 mm/min	97	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	1	%	ISO 527
Tensile Strain, break, 5 mm/min	1	%	ISO 527
Tensile Modulus, 1 mm/min	10700	MPa	ISO 527
Flexural Stress, break, 2 mm/min	180	MPa	ISO 178
Flexural Modulus, 2 mm/min	9100	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	89	J/m	ASTM D 256
Izod Impact, notched, -30°C	75	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	9	J	ASTM D 3763
Izod Impact, notched 80104 +23°C	9	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	7	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	21	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	156	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	191	°C	ASTM D 648
CTE, -40°C to 150°C, flow	2.03E-05	1/°C	ASTM E 831
CTE, -40°C to 150°C, xflow	1.02E-04	1/°C	ASTM E 831
CTE, 23°C to 80°C, flow	2.03E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	1.02E-04	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	156	°C	ISO 306
Vicat Softening Temp, Rate B/120	156	°C	ISO 306
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.64	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.6	%	S-Plastics Method
Melt Flow Rate, 250°C/5.0 kgf	26	g/10 min	ASTM D 1238
Density	1.64	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.07	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.06	%	ISO 62
Melt Volume Rate, MVR at 250°C/5.0 kg	18	cm³/10 min	ISO 1133
Source GMD, last updated:04/26/2007

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	110 - 120	°C
Drying Time	2 - 4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250 - 270	°C
Nozzle Temperature	240 - 260	°C
Front - Zone 3 Temperature	245 - 265	°C
Middle - Zone 2 Temperature	240 - 255	°C
Rear - Zone 1 Temperature	230 - 245	°C
Hopper Temperature	40 - 60	°C
Mold Temperature	40 - 100	°C
Source GMD, last updated:04/26/2007