LNP Stat Kon

S-Plastic Stat-kon DE0049F resin is a carbon fiber filled polycarbonate with flame retardant and superior molding characteristics. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 137 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 137 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 1.9 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 1.9 % ASTM D 638 Tensile Modulus, 50 mm/min 13420 MPa ASTM D 638 Flexural Stress,

S-Plastic Stat-kon DE0049 resin is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break, 5 mm/min 147 MPa ISO 527 Tensile Strain, break, 5 mm/min 1.4 % ISO 527 Tensile Modulus, 1 mm/min 13700 MPa ISO 527 Flexural Stress, break, 2 mm/min 83 MPa ISO 178 Flexural Modulus, 2 mm/min 2800 MPa ISO 178 IMPACT Value Unit Standard Izod Impact, notched 80*10*4

S-Plastic Stat-kon DE004 resin is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 120 MPa ASTM D 638 Tensile Strain, break 2.2 % ASTM D 638 Tensile Modulus, 50 mm/min 10890 MPa ASTM D 638 Flexural Stress 196 MPa ASTM D 790 Flexural Modulus 9790 MPa ASTM D 790 Tensile Stress, break 114 MPa ISO 527 Tensile Strain, break 1.6 % ISO 527

S-Plastic Stat-kon DE003Z resin is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: ​Property TYPICAL PROPERTIES (1) IMPACT Value Unit Standard Instrumented Impact Energy @ peak, 23°C 15 J ASTM D 3763 Multiaxial Impact 104 J ISO 6603 THERMAL Value Unit Standard HDT, 1.82 MPa, 3.2mm, unannealed 141 °C ASTM D 648 CTE, -40°C to 40°C, flow 1.26E-05 1/°C ASTM E 831 CTE, -40°C to 40°C, xflow 7.02E-05 1/°C ASTM E 831 CTE, -40°C to

S-Plastic Stat-kon DE003P resin is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 121 MPa ASTM D 638 Tensile Strain, break 1.7 % ASTM D 638 Tensile Modulus, 50 mm/min 11160 MPa ASTM D 638 Flexural Stress 193 MPa ASTM D 790 Flexural Modulus 9920 MPa ASTM D 790 Tensile Stress, break 110 MPa ISO 527 Tensile Strain, break 1.4 % ISO 527

S-Plastic Stat-kon DE003M resin is a compound based on polycarbonate and carbon fiber. Characteristics of this grade include Milled Carbon ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 101 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 101 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 2.8 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 2.9 % ASTM D 638 Tensile Modulus, 50 mm/min 8470 MPa ASTM D 638 Flexural

S-Plastic Stat-kon DE003ER resin is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 109 MPa ASTM D 638 Tensile Strain, break 2.1 % ASTM D 638 Tensile Modulus, 50 mm/min 8780 MPa ASTM D 638 Flexural Stress 182 MPa ASTM D 790 Flexural Modulus 7790 MPa ASTM D 790 Tensile Stress, break 108 MPa ISO 527 Tensile Strain, break 2 %

S-Plastic Stat-kon DE003E resin is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break, 5 mm/min 134 MPa ISO 527 Tensile Strain, break, 5 mm/min 1.6 % ISO 527 Tensile Modulus, 1 mm/min 12200 MPa ISO 527 Flexural Stress, yield, 2 mm/min 184 MPa ISO 178 Flexural Modulus, 2 mm/min 10800 MPa ISO 178 IMPACT Value Unit Standard Izod Impact,

S-Plastic Stat-kon DE0039 resin is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Flame Retardant. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yield 118 MPa ASTM D 638 Tensile Stress, break 118 MPa ASTM D 638 Tensile Strain, yield 2.4 % ASTM D 638 Tensile Strain, break 2.4 % ASTM D 638 Tensile Modulus, 50 mm/min 9650 MPa ASTM D 638 Flexural Stress 144 MPa ASTM D 790

S-Plastic Stat-kon DE002P resin is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 115 MPa ASTM D 638 Tensile Strain, break 2.4 % ASTM D 638 Tensile Modulus, 50 mm/min 8680 MPa ASTM D 638 Flexural Stress 185 MPa ASTM D 790 Flexural Modulus 7370 MPa ASTM D 790 Tensile Stress, break 118 MPa ISO 527 Tensile Strain, break 2.5 % ISO 527

S-Plastic Stat-kon DE002ER resin is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 100 MPa ASTM D 638 Tensile Strain, break 2.8 % ASTM D 638 Tensile Modulus, 50 mm/min 6960 MPa ASTM D 638 Flexural Stress 165 MPa ASTM D 790 Flexural Modulus 6130 MPa ASTM D 790 Tensile Stress, break 102 MPa ISO 527 Tensile Strain, break 3.3 %

S-Plastic Stat-kon DE002E resin is a compound based on Polycarbonate resin containing Carbon Fiber. Added features include; Easy Molding. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break, 5 mm/min 117 MPa ISO 527 Tensile Strain, break, 5 mm/min 1.8 % ISO 527 Tensile Modulus, 1 mm/min 8600 MPa ISO 527 Flexural Stress, yield, 2 mm/min 157 MPa ISO 178 Flexural Stress, break, 2 mm/min 150 MPa ISO 178 Flexural Strain, break, 2 mm/min 2.9 % ISO 178

S-Plastic Stat-kon DE0029EF resin is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Easy Molding. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 114 MPa ASTM D 638 Tensile Strain, break 2.3 % ASTM D 638 Tensile Modulus, 50 mm/min 8890 MPa ASTM D 638 Flexural Stress 180 MPa ASTM D 790 Flexural Modulus 7650 MPa ASTM D 790 Tensile Stress, break 117 MPa ISO 527 Tensile

S-Plastic Stat-kon DE0029EC resin is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Retardant. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 110 MPa ASTM D 638 Tensile Strain, break 2.7 % ASTM D 638 Tensile Modulus, 50 mm/min 8270 MPa ASTM D 638 Flexural Stress 179 MPa ASTM D 790 Flexural Modulus 7580 MPa ASTM D 790

S-Plastic Stat-kon DE0029 resin is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 104 MPa ASTM D 638 Tensile Strain, break 5.9 % ASTM D 638 Flexural Stress 158 MPa ASTM D 790 Flexural Modulus 7580 MPa ASTM D 790 Tensile Stress, break 104 MPa ISO 527 Tensile Strain, break 6.2 %

S-Plastic Stat-kon DE0026E resin is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yield, 5 mm/min 117 MPa ISO 527 Tensile Strain, yield, 5 mm/min 2.7 % ISO 527 Tensile Modulus, 1 mm/min 8000 MPa ISO 527 Flexural Stress, yield, 2 mm/min 182 MPa ISO 178 Flexural Modulus, 2 mm/min 10900

S-Plastic Stat-kon DE0026 resin is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Flame Retardant, Electrically Conductive. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break, 5 mm/min 111 MPa ISO 527 Tensile Strain, break, 5 mm/min 2.8 % ISO 527 Flexural Stress, break, 2 mm/min 153 MPa ISO 178 Flexural Modulus, 2 mm/min 6000 MPa ISO 178 IMPACT Value Unit Standard Izod

S-Plastic Stat-kon DE0021E resin is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Easy Molding. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 114 MPa ASTM D 638 Tensile Strain, break 1.8 % ASTM D 638 Tensile Modulus, 50 mm/min 9160 MPa ASTM D 638 Flexural Stress 170 MPa ASTM D 790 Flexural Modulus 8210 MPa ASTM D 790 Tensile Stress, break 112 MPa ISO 527 Tensile

S-Plastic Stat-kon DE002 resin is a Polycarbonate containing Carbon Fiber ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 97 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 7.5 % ASTM D 638 Tensile Modulus, 50 mm/min 11140 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 159 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 7460 MPa ASTM D 790 Tensile Stress, break, 5 mm/min 97 MPa ISO 527 Tensile Strain,

S-Plastic Stat-kon DDF029 resin is a compound based on Polycarbonate resin containing Carbon Powder, Glass Fiber, Flame Retardant. Added features of this material include: Electrically Conductive. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 81 MPa ASTM D 638 Tensile Strain, break 2.9 % ASTM D 638 Tensile Modulus, 50 mm/min 4480 MPa ASTM D 638 Flexural Stress 132 MPa ASTM D 790 Flexural Modulus 4410 MPa ASTM D 790 Tensile Stress, break 81