LNP Stat Kon

S-Plastic Stat-kon AE0039 resin is LNP STAT-KON* AE0039 is a compound based on Acrylonitrile Butadiene Styrene resin containing Carbon Fiber, Flame Retardant. ​PropertyTYPICAL PROPERTIES (1) MECHANICALValueUnitStandardTensile Stress, break103MPaASTM D 638Tensile Strain, break1.5%ASTM D 638Tensile Modulus, 50 mm/min11230MPaASTM D 638Flexural Stress151MPaASTM D 790Flexural Modulus8270MPaASTM D 790Tensile Stress, break65MPaISO 527Tensile Strain, break2.3%ISO 527Tensile Modulus, 1 mm

S-Plastic Stat-kon AE002 resin is LNP* Stat-kon* AE002 is a compound based on Acrylonitrile Butadiene Styrene resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 78 MPa ASTM D 638 Tensile Strain, break 1.5 % ASTM D 638 Tensile Modulus, 50 mm/min 7230 MPa ASTM D 638 Flexural Stress 117 MPa ASTM D 790 Flexural Modulus 7030 MPa ASTM D 790 IMPACT Value

S-Plastic Stat-kon AD000Z resin is LNP* Stat-Kon AD000Z is a compound based on ABS resin with carbon powder. Grade characteristics: a statically conductive extrusion grade. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 41 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 37 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 1.9 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 2.5 % ASTM D 638 Tensile Modulus, 50 mm

S-Plastic Stat-kon AD000 resin is ABS, Carbon,Property ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 31 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 29 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 2 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 6.4 % ASTM D 638 Tensile Modulus, 50 mm/min 2380 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 59 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm

S-Plastic Stat-kon 9X06519 resin is a compound based on Cyclic Olefinic Copolymer resin containing Carbon Fiber. Added features of this material include: Clean Compounding System. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 74 MPa ASTM D 638 Tensile Strain, break 0.5 % ASTM D 638 Tensile Modulus, 50 mm/min 16040 MPa ASTM D 638 Flexural Stress 158 MPa ASTM D 790 Flexural Modulus 16680 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact,

S-Plastic Stat-kon 9X04323 resin is a compound based on Noryl GTX resin,Added features of this material include: Electrically Conductive. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 59 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 56 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 3.7 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 3.7 % ASTM D 638 Tensile Modulus, 50 mm/min 2760 MPa ASTM D 638 Flexural

S-Plastic Stat-kon 9X02785 resin is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yield 64 MPa ASTM D 638 Tensile Strain, break 4 % ASTM D 638 Tensile Modulus, 50 mm/min 2890 MPa ASTM D 638 Flexural Stress 103 MPa ASTM D 790 Flexural Modulus 2890 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact,

S-Plastic Stat-kon 9X02785 resin is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive. ​Property TYPICAL PROPERTIES (1) 　 　 　 MECHANICAL Value Unit Standard Tensile Stress, yield 64 MPa ASTM D 638 Tensile Strain, break 4 % ASTM D 638 Tensile Modulus, 50 mm/min 2890 MPa ASTM D 638 Flexural Stress 103 MPa ASTM D 790 Flexural Modulus 2890 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact,