S-Plastic Thermocomp

S-Plastic Thermocomp IC006 resin is a compound based on Nylon 6/12 resin containing Carbon Fiber. Added features of this material include:Electrically Conductive. ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 201 MPa ASTM D 638 Tensile Stress, break 201 MPa ASTM D 638 Tensile Strain, yield 2.2 % ASTM D 638 Tensile Strain, break 2.2 % ASTM D 638 Tensile Modulus, 50 mm/min 17920 MPa ASTM D 638 Flexural Stress 262 MPa ASTM D 790 Flexural Modulus 12410 MPa ASTM D 790

S-Plastic Thermocomp IB008 resin is a compound based on Nylon 6/12 resin containing Glass Bead. ​Property MECHANICAL Value Unit Standard Tensile Stress, break, 5 mm/min 74 MPa ISO 527 Tensile Strain, break, 5 mm/min 3.6 % ISO 527 Flexural Stress, break, 2 mm/min 103 MPa ISO 178 Flexural Modulus, 2 mm/min 3900 MPa ISO 178 IMPACT Value Unit Standard Izod Impact, unnotched 80*10*4 +23°C 15 kJ/m² ISO 180/1U Izod Impact, notched 80*10*4 +23°C 4 kJ/m² ISO 180/1A THERMAL Value Unit

S-Plastic Thermocomp HX05073 resin is a compound based on Nylon 11 resin containing Glass Fiber. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 134 MPa ASTM D 638 Tensile Strain, break 6.2 % ASTM D 638 Tensile Modulus, 50 mm/min 7370 MPa ASTM D 638 Flexural Stress 195 MPa ASTM D 790 Flexural Modulus 6200 MPa ASTM D 790 Tensile Stress, break 130 MPa ISO 527 Tensile Strain, break 6.3 % ISO 527 Tensile Modulus, 1 mm/min 7080 MPa ISO 527 Flexural Stress 193 MPa ISO

S-Plastic Thermocomp HX0309C resin is a compound based on PA11 resin containing Metal Filler. Added features include: Clean Compound ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 50 mm/min 33 MPa ISO 527 Tensile Strain, break, 50 mm/min 42 % ISO 527 Tensile Modulus, 1 mm/min 1500 MPa ISO 527 Flexural Stress, yield, 2 mm/min 51 MPa ISO 178 Flexural Modulus, 2 mm/min 1900 MPa ISO 178 IMPACT Value Unit Standard Izod Impact, unnotched 80*10*4 +23°C 75 kJ/m² ISO 180

S-Plastic Thermocomp HH0420A resin is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 40 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 40 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 1.3 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 1.3 % ASTM D 638 Tensile Modulus, 50 mm/min 5770 MPa ASTM D 638 Flexural Stress,

S-Plastic Thermocomp HH00ASU resin is a compound based on PA11 resin containing Glass Fiber. Added features include; Heat Stabilized, UV-Stabilized. ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 5 mm/min 158 MPa ISO 527 Tensile Strain, break, 5 mm/min 5.6 % ISO 527 Tensile Modulus, 1 mm/min 9800 MPa ISO 527 Flexural Stress, yield, 2 mm/min 223 MPa ISO 178 Flexural Modulus, 2 mm/min 10300 MPa ISO 178 IMPACT Value Unit Standard Izod Impact, unnotched 80*10*4 +23°C

S-Plastic Thermocomp HF008 resin is a compound based on Nylon 11 resin containing Glass Fiber. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 122 MPa ASTM D 638 Tensile Strain, break 4.9 % ASTM D 638 Tensile Modulus, 50 mm/min 9280 MPa ASTM D 638 Flexural Stress 220 MPa ASTM D 790 Flexural Modulus 8480 MPa ASTM D 790 Tensile Stress, break 123 MPa ISO 527 Tensile Strain, break 3.9 % ISO 527 Tensile Modulus, 1 mm/min 7600 MPa ISO 527 Flexural Stress 192 MPa ISO 178

S-Plastic Thermocomp HF006EU resin is a compound based on PA 11 resin containing Glass Fiber. Added features include: Easy Molding, UV-Stabilized. ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 5 mm/min 117 MPa ISO 527 Tensile Stress, break, 5 mm/min 116 MPa ISO 527 Tensile Strain, yield, 5 mm/min 6 % ISO 527 Tensile Modulus, 1 mm/min 7100 MPa ISO 527 Flexural Stress, yield, 2 mm/min 169 MPa ISO 178 Flexural Modulus, 2 mm/min 5600 MPa ISO 178 IMPACT Value Unit

S-Plastic Thermocomp HF004 resin is a compound based on Nylon 11 resin containing Glass Fiber. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 81 MPa ISO 527 Tensile Strain, break 12.2 % ISO 527 Tensile Modulus, 1 mm/min 3670 MPa ISO 527 Flexural Stress 100 MPa ISO 178 Flexural Modulus 3540 MPa ISO 178 IMPACT Value Unit Standard Izod Impact, unnotched 80*10*4 +23°C 75 kJ/m² ISO 180/1U Izod Impact, notched 80*10*4 +23°C 15 kJ/m² ISO 180/1A THERMAL Value Unit

S-Plastic Thermocomp HB006 resin is a compound based on Nylon 11 resin containing Glass Bead. ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 45 MPa ASTM D 638 Tensile Stress, break 43 MPa ASTM D 638 Tensile Strain, yield 23.2 % ASTM D 638 Tensile Strain, break 20 % ASTM D 638 Tensile Modulus, 50 mm/min 1960 MPa ASTM D 638 Flexural Stress 55 MPa ASTM D 790 Flexural Modulus 1920 MPa ASTM D 790 Tensile Stress, yield 46 MPa ISO 527 Tensile Stress, break 41 MPa ISO 527

S-Plastic Thermocomp GX94043L resin is a compound based on Polysulfone resin containing Mineral. ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 5 mm/min 72 MPa ISO 527 Tensile Strain, break, 5 mm/min 4.3 % ISO 527 Tensile Modulus, 1 mm/min 3500 MPa ISO 527 Flexural Stress, yield, 2 mm/min 119 MPa ISO 178 Flexural Modulus, 2 mm/min 3800 MPa ISO 178 IMPACT Value Unit Standard Izod Impact, unnotched 80*10*4 +23°C 50 kJ/m² ISO 180/1U Izod Impact, notched 80*10*4 +23

S-Plastic Thermocomp GX061104 resin is a compound based on Polysulfone resin. ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 50 mm/min 73 MPa ISO 527 Tensile Stress, break, 50 mm/min 53 MPa ISO 527 Tensile Strain, yield, 50 mm/min 5.9 % ISO 527 Tensile Modulus, 1 mm/min 2500 MPa ISO 527 Flexural Stress, yield, 2 mm/min 113 MPa ISO 178 Flexural Modulus, 2 mm/min 2600 MPa ISO 178 IMPACT Value Unit Standard Izod Impact, unnotched 80*10*4 +23°C NB kJ/m² ISO 180/1U

S-Plastic Thermocomp GX05482 resin is a compound based on Polysulfone resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 72 MPa ASTM D 638 Tensile Strain, break 1 % ASTM D 638 Tensile Modulus, 50 mm/min 9990 MPa ASTM D 638 Flexural Stress 117 MPa ASTM D 790 Flexural Modulus 9650 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C 267 J/m ASTM D

S-Plastic Thermocomp GX05053 resin is a compound based on Polysulfone blend resin containing Glass Fiber. ​PropertyMECHANICALValueUnitStandardTensile Stress, yield, 5 mm/min94MPaISO 527Tensile Strain, break, 5 mm/min3.6%ISO 527Tensile Modulus, 1 mm/min4700MPaISO 527Flexural Stress, yield, 2 mm/min147MPaISO 178Flexural Modulus, 2 mm/min4400MPaISO 178IMPACTValueUnitStandardIzod Impact, unnotched 80*10*4 +23°C45kJ/m²ISO 180/1UIzod Impact, notched 80*10*4 +23°C7kJ/m²ISO 180

S-Plastic Thermocomp GF008 resin is a compound based on Polysulfone resin containing Glass Fiber. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 108 MPa ASTM D 638 Tensile Strain, break 1.4 % ASTM D 638 Tensile Modulus, 50 mm/min 11650 MPa ASTM D 638 Flexural Stress 158 MPa ASTM D 790 Flexural Modulus 11700 MPa ASTM D 790 Tensile Stress, break 113 MPa ISO 527 Tensile Strain, break 1.4 % ISO 527 Flexural Stress 164 MPa ISO 178 Flexural Modulus 9900 MPa ISO 178

S-Plastic Thermocomp GF006 resin is a compound based on Polysulfone resin containing Glass Fiber. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 104 MPa ASTM D 638 Tensile Strain, break 2 % ASTM D 638 Tensile Modulus, 50 mm/min 8820 MPa ASTM D 638 Flexural Stress 156 MPa ASTM D 790 Flexural Modulus 8270 MPa ASTM D 790 Tensile Stress, break 100 MPa ISO 527 Tensile Strain, break 1.9 % ISO 527 Tensile Modulus, 1 mm/min 8420 MPa ISO 527 Flexural Stress 150 MPa ISO 178

S-Plastic Thermocomp GF004 resin is a compound based on Polysulfone resin containing Glass Fiber. ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 91 MPa ASTM D 638 Tensile Stress, break 91 MPa ASTM D 638 Tensile Strain, yield 2.3 % ASTM D 638 Tensile Strain, break 2.3 % ASTM D 638 Tensile Modulus, 50 mm/min 6200 MPa ASTM D 638 Flexural Stress 137 MPa ASTM D 790 Flexural Modulus 6200 MPa ASTM D 790 Flexural Stress 145 MPa ISO 178 Flexural Modulus 6000 MPa ISO 178

S-Plastic Thermocomp GF003 resin is a compound based on Polysulfone resin containing Glass Fiber. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 85 MPa ASTM D 638 Flexural Modulus 4890 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C 587 J/m ASTM D 4812 Izod Impact, notched, 23°C 58 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 1.82 MPa, 3.2mm, unannealed 179 °C ASTM D 648 PHYSICAL Value Unit Standard Density 1.35 g/cm³ ASTM D 792 Source

S-Plastic Thermocomp DF006LXN resin is a compound based on Polycarbonate resin containing Glass Fiber. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 114 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 2.7 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 3.2 % ASTM D 638 Tensile Modulus, 50 mm/min 8630 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 149 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm

S-Plastic Thermocomp GC006XXZ resin is PEI, Carbon Fiber, ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 104 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 137 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 0.7 % ASTM D 638 Tensile Modulus, 50 mm/min 35160 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 191 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 16130 MPa ASTM D 790 Tensile Stress, break, 5 mm/min 136 MPa