Die Steel Bar

AISI/SAE D3 Die Steel Bar DIN/EN X210Cr12 BS X210Cr12 In general, the applications of D3 tool steel resemble those of D2 but it should be remembered that D3 has better wear resistance of the two steels and is preferred for such items as shear blades. Owing to its higher wear resistance, D3 tool steel is slightly more difficult to grind than D2.D3 exhibits excellent stability in heat treatment, holding size almost as well as the air-hardening, high-carbon, high-chromium die

H13 Die Steel Bar 6.0mm-500mm DIN/EN X40CrMoV5-1 ASTM A681-2008 H13 is widely used for aluminum and zinc casting dies, as well as for aluminum extrusion, aluminum die casting and press tooling. This grade is ideal for a range of hot work and cold work applications—particularly hot work applications where drastic cooling is required throughout its operation. For hot work applications, H13 is used in the hardness range of HRC 38 to 48. The usual hardness range for die casting

ASTM A681-2008 Die Steel Bar 6.0mm-500mm DIN/EN X40CrMoV5-1 H13 has high hardenability and hot crack resistance because it contains higher content of carbon and vanadium, good wear resistance, relatively weakened toughness, good heat resistance, better strength and hardness at higher temperatures, high wear resistance and toughness, excellent comprehensive mechanical properties and high tempering stability. Supply Form & Size Form of Supply Size(mm) Length(mm) Round bar 6.0mm

D2 Die steel ASTM A681 - 2008 Hot rolled / bright round bar D2 steel has high wear resistance, micro-deformation cold working die steel, and wind-hardened tool steel, with carbon content up to 1.5%, chromium content up to 11.5%, and hardness up to 60HRC after heat treatment. D2 steel, such as silicon steel sheet punching die, cold cutting scissors, trimming die, etc. High wear resistance, vacuum heat treatment to HRC60 ° - 62 °, excellent processing performance. Supply Form &

SKD61 Die Steel Bar AISI/SAE H13 BS X40CrMoV5-1 SKD61 has good toughness and high temperature fatigue resistance, can withstand temperature fusion, suitable for long-term work at high temperature, and has good cutting and polishing performance. SKD61 is smelted by electric furnace and remelted by electroslag, and the steel is purer and tougher. The purpose is suitable for making aluminum, zinc, copper alloy extrusion dies, die-casting molds, hot forging dies, and hot shear

Die Steel Bar JIS G4404-2006 Cr12MoV SKD11 SKD11 (alloy tool steel): High-Carbon High-Chromium alloy steel with high hardness (appropriate toughness) and tempering hardening effect. Examples like stamping mold, plastic mold and other multi-function items.After quenching, residual austenite is about 13% to 20%. Equivalent Grades: GB Cr12MoV, JIS SKD11, AISI/SAE D3, DIN 2X165CrMoV12. SKD11 is the tool steel, die steel, and high carbon steel possessing high hardness, strength

SKD11 Die Steel Bar JIS G4404-2006 Cr12MoV SKD11 is a general cold work die steel with high wear resistance and toughness, high carbon and high chromium alloy tool steel and vacuum degassed refined steel, with pure steel, good hardenability with good hardenability and small quenching deformation. The steel is spheroidized annealed and softened, with good processability, fine and uniform carbide particles, and no need to worry about the special addition of quenching cracking

Die Steel Bar DIN/EN X210Cr12 BS X210Cr12 AISI/SAE D3 D3 is the cold work die steel with the most superior abrasiveness. The heat treatment effect is stable. Steel for deep drawing dies cold forging dies..... Resistance welding electrode: chromium-zirconium copper guarantees performance by combining heat treatment and cold working, and it can obtain the best mechanical and physical properties. High carbon, high chromium type Leystenite cold work die steel, with good