Stainless Steel Flat Bar

304L stainless steel flat bar 304L is the low carbon version of 304. It is used in heavy gauge components for improved weldability. 304L has a carbon maximum is 0.030. Austenitic Cr-Ni stainless steel. Better corrosion resistance than 302. High ductility, excellent drawing, forming, and spinning properties. Essentially non-magnetic, becomes slightly magnetic when cold worked. Low carbon content means less carbide precipitation in the heat-affected zone during welding and a

304 stainless steel is the most versatile and widely used stainless steel. 304 stainless steel is an austenitic grade that can be severely deep drawn. This property has resulted in 304 being the dominant grade used in applications like sinks and saucepans. It is also widely used in springs, screws, architectural panelling, tubing, brewery, food, dairy and pharmaceutical production equipment. ElementType 304 (Wt.%) Carbon: 0.08 max Manganese: 2.00 max. Phosphorus: 0.045 max.

201 is part of the 200 series of austenitic stainless steel. 201 is used to produce a range of household appliances, including sinks, cooking utensils, washing machines, windows, and doors. It is also used in automotive trim, decorative architecture, railway cars, trailers, and clamps. It is not recommended for structural outdoor applications because of its susceptibility to pitting and crevice corrosion. ElementType 201 (Wt.%) Carbon: 0.15 max Manganese: 5.50-7.50 max.

202 stainless steel flat bar Grade 202 stainless steel is a type of Cr-Ni-Mn stainless with similar properties to A240/SUS 302 stainless steel. The toughness of grade 202 at low temperatures is excellent.It is one of the most widely used precipitation hardening grades, and possesses good corrosion resistance, toughness, high harness, and strength. ElementType 202 (Wt.%) Carbon: 0.15 max Manganese: 7.50-10.00 max. Phosphorus: 0.06 max. Sulfur: 0.03 max. Silicon 1.00 max.

309 is an austenitic chromium-nickel stainless steel known for its high corrosion resistance and strength. 309 has the same machining properties as 304, and can be roll formed, stamped, and drawn easily. Due to its properties, especially its ability to work under high-temperatures, you will find 309 in a wide variety of applications including: Boiler baffles, furnace components, oven lining, fireboxes, kiln Liners, sulfite liquor handling equipment, carbuizing-annealing boxes

316L stainless steel angle bar 316L austenitic stainless steel is a low carbon version of 316 . The low carbon helps improve weldability as compared to the 316 as well as improved corrosion resistance. The added Molybdenum in 316L gives this grade much better pitting resistance than the traditional 304L stainless. This alloy is one of the most widely used stainless steels showing up in just about every industry and is often used in seawater applications due to the pitting

321 stainless steel flat bar 321 SS is a titanium stabilized austenitic chromium-nickel stainless steel which was developed to provide an 18-8 type alloy with improved intergranular-corrosion resistance. This material is stabilized against chromium carbide formation by the addition of titanium. Since titanium has a stronger affinity for carbon than chromium, titanium carbide precipitates within the grains instead of forming at the grain boundaries. 321 stainless steel should

410/410s stainless steel flat bar 410 stainless steels are general-purpose martensitic stainless steels containing 11.5% chromium, which provide good corrosion resistance properties. However, the corrosion resistance of 410 steels can be further enhanced by a series of processes such as hardening, tempering and polishing. Quenching and tempering can harden 410 steels. They are generally used for applications involving mild corrosion, heat resistance and high strength. 410

2205 stainless steel flat bar Duplex 2205 is a two-phase, ferritic, austenitic 22% chromium, 3% molybdenum, 5 to 6% nickel alloyed stainless steel. It is the most widely used duplex stainless steel grade and is characterized by high yield strength, double that of the standard austenitic stainless steel grades. It also demonstrates good fatigue strength, as well as outstanding resistance to stress corrosion cracking, crevice, pitting, erosion, and general corrosion in severe

904L stainless steel flat bar 904L is an austenitic stainless steel. In comparison to 316L, its molybdenum addition gives it superior resistance to localized attack (pitting and crevice corrosion) by chlorides and greater resistance reducing acids and in particular its copper addition gives it useful corrosion resistance to all concentrations of sulphuric acid. Its high alloying content also gives it greater resistance to chloride stress corrosion cracking, but it is still