SUS632 PH15-7Mo EN 1.4532 Cold Rolled Stainless Steel Strip In Coil​

Precipitation hardening stainless steel SUS632, PH15-7Mo, EN 1.4532, DIN X8CrNiMoAl15-7-2 

with high strength and hardness, good corrosion resistance, and satisfactory formability.

PH15-7Mo stainless alloy is particularly beneficial for a wide range of applications that

include retaining rings, springs, diaphragms, aircraft bulkheads, welded and brazed honeycomb 

paneling and other aircraft components requiring high strength at elevated temperatures.

Chemical composition % weight

Heat treatment 

PH15-7Mo Stainless Steel requires three essential steps in heat treating:

1) austenite conditioning, 

2) cooling to transform the austenite to martensite

and 3) precipitation hardening.

The material normally is supplied from the mill in Condition A.

After fabrication, an austenite conditioning treatment is followed by a transformation treatment to

either Condition T or Condition R 100. Then the material is precipitation
hardened to either Condition TH 1050 or Condition RH 950 to develop fully useable properties.
To obtain the highest mechanical properties in this alloy, Condition A material is transformed to

martensite at the mill by cold reduction to Condition C.

After fabrication by the user, hardening to Condition CH 900 is accomplished with a single low-temperature heat treatment.

Specifications

AMS 5520 Sheet, Strip and Plate
ASTM A 693 Plate, Sheet and Strip (Listed as Grade 632-UNS S15700)

For Details, please Contact

WUXI GUANGLU Special Steel Co., Ltd.

Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs

Tel: +86 510 81812873

Email: export@guanglusteel.com