ASME SB111 C68700 Aluminum Brass Seamless Tube u tube heat exchanger
ASME SB111 C68700 Aluminum Brass Seamless Tube u tube heat exchanger
This specification covers U-bend seamless condenser, evaporator, and heat exchanger tubes of copper and copper alloys up to 2 in., inclusive, in diameter. Tubes for this application are normally made from the following copper or copper alloys:
Copper Alloy Tube----Aluminum Brass Tube
Aluminum Brass Tube is a copper zinc alloy containing aluminum and small amount of arseric which is added as an inhibitor against dezincification. Inhibited Aluminum Brass resists the action of high velocity salt and brackish water and is commonly used for condenser tube.
The outstanding characteristic of Aluminum Brass is th high resistance to impringement attack.
Aluminum Brass tubes are highly accepted and one of the extensively used material for various industrial applications.
Product Range
• Outside diameter : 5.0 mm(min) ~ 65 mm(max)
• Wall thickness : 0.5mm(Min.)
• Length : 27,000mm(Max.)
• Product capacity per month : 500 M.T.
• U-bend tube (smallest bending radius ≥ 2 x tube O.D.)
Application :
Steam Ejector, Intor and After Condensers, Grand steam condensers, Feed Water Evaporators for Petrochemical, Ship-building, Power plants and Desalination plants etc.
Chemical composition
| Standard | Class | Chemical composion(%) | Related standards | ||||||||||||||
| Cu | Zn | Pb | Fe | P | Sn | Ni | Mn | Al | As | Other | KS | JIS | ASTM | BS | DIN | ||
| ASTM | 1 | 76.0-79.0 | Rem. | 0.07 Max. | 0.06 Max. | 1.8-2.5 | 0.02-0.10 | D5301 C6870 | H3300 C6870 | B111 C68700 | 2871 CZ110 | 1785 CuZn20Al | |||||
| 2 | 76.0-79.0 | Rem. | 0.05 Max. | 0.05 Max. | 1.8-2.5 | 0.02-0.06 | Si 0.2-0.5 | C6871 | C6871 | C68700 | 2871 CZ110 | CuZn20Al | |||||
| 3 | 76.0-79.0 | Rem. | 0.07 Max. | 0.06 Max. | 0.20 - 1.0 | 0.20-Max. | 1.8-2.5 | 0.02-0.06 | Cr0.10 Max. | C6872 | C6872 | C68700 | 2871 CZ110 | CuZn20Al | |||
Mechanical properties
| Standard | Temper | Designation | Tensile test | Hardness test | |||||
| Outside diameter(mm) | Thickness (mm) | Tensile strength min ksi | Elongation in 2in., min% | Yield strength min ksi | Rockwell hardness | ||||
| HR30T | HR15T | ||||||||
| ASTM | O61 | C68700 | 5-50 | 0.8-0.10 | 50 | - | 18 | - | - |
| JIS | O61 | C6871T-O | 50-250 | 0.8-0.10 | 36Min. | 40Min. | 13Min. | - | - |
| C6872T-O, C687TS-O | 50-250 | 0.8-0.10 | 36Min. | 40Min. | 13Min. | - |
- |
||
Additional Testing
- Dye penetrant of 'U' bend area
- PMI testing
- Heat Treatment
Heat Treatment
We are equipped to carry out heat treatment of bends plus a minimum 150mm of leg.
Heat Treatment Equipment
- Heat treatment equipment is computer controlled with the added facility of data recording.
- An argon protective atmopshere is used inside stainless and special alloy tubes during heat treatment.
- We can provide all types of annealing; solution annealing and stress relieving.
Chemical Composition
|
| Materials - U-Bent Tube | |
|---|---|
| Carbon Steel | SA 179 / A 179 |
| Carbon Steel | SA 210 / A 210 |
| Carbon Steel | SA 334 / A 334 |
| Stainless Steel | SA 213 / A 213 |
| SA249 / A249 | |
| SA268 / A268 | |
| SA688 / A688 | |
| Duplex Stainless Steel | SA 789 / A 789 |
| Copper & Cu Alloys | SB 111 / B 111 |
| Titanium & Ti Alloys | SB 338 / B 338 |
| For different materials please contact our sales department. | |
Mechanical Properties
| Physical Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 8.8-8.94 | 25 | |
| Poisson's Ratio | 0.34 | 25 | |
| Elastic Modulus (GPa) | 117 | 25 | |
| Tensile Strength (Mpa) | 414 | 25 | Tube |
| Yield Strength(Mpa) | 186 | ||
| Elongation (%) | 55 | ||
| Reduction in Area (%) | |||