MoSi2 High Temperature Heating Element Of Glass Furnace 1800 ℃​

MoSi2 Heating Element Application:

MoSi2 Heating Element are extensively used in the industries of metallurgy, glass, ceramic refractory,crystal electronic device, industrial furnace manufacture, etc.. It is an essential ideal element when the products are sintering in the high temperature.

Attention: MoSi2 elements can not be used in 400 to 700 °C for a long time, otherwise, it will be powered and damaged due to strong oxidizing action in low temperature.

When you place order, please tell us following data:

d = the diameter of hot zone

c = the diameter of cold zone

Le = the length of hot zone

Lu = the length of cold zone

A = the distance between two terminals

Examples:

U-Shape, Material Grade 1800, D1=3mm, D2=6mm, Le=140mm, Lu=125mm, A=25mm

Specify as: MS18U, 3/6 x 140 x 125 x 25

Product Parameters:

1. Physical Properties of MoSi2 Heating Element

2. Chemical Properties of Physical Properties of MoSi2 Heating Element

Oxygen-resistance under high temperature: in oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of element owing to the high temperature combustion, which prevent Mosi2 from oxidizing more. When the element temperature is higher than 1700 °C, the film becomes melting. It’s not suitable for long time use in the temperature range of 400-700°C, otherwise, the element will be powdering for the strong oxidation under low temperature.

3. Max temperatures of MoSi2 Heating Element in Different Atmospheres